The microstructure of the as-cast 7A55 aluminum alloy and its evolution during homogenization were investigated by means of optical microscopy （OM）, scanning electron microscopy （SEM）, energy dispersive spectrosco...The microstructure of the as-cast 7A55 aluminum alloy and its evolution during homogenization were investigated by means of optical microscopy （OM）, scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDS）, X-ray diffraction （XRD）, and differential scanning calorimetry （DSC） analysis. The results indicate that the microstructure of the as-cast 7A55 aluminum alloy mainly consists of the dendritic network of aluminum solid solution, Al/AIZnMgCu eutectic phases, and intermetaUic compounds MgZn2, Al2CuMg, Al7Cu2Fe, and Al23CuFe4. After homogenization at 470℃ for 48 h, Al/AlZnMgCu eutectic phases are dissolved into the matrix, and a small amount of high melting-point secondary phases were formed, which results in an increasing of the starting melting temperature of 7A55 aluminum alloy The high melting-point secondary phases were eliminated mostly when the homogenization time achieved to 72 h. Therefore, the reasonable homogenization heat treatment process for 7A55 aluminum alloy ingots was chosen as 470℃/72 h.展开更多
基金financially supported by the National Key Technologies R&D Program of China (No.2007BAE38B06)the National Natural Science Foundation of China (No.50904010)
文摘The microstructure of the as-cast 7A55 aluminum alloy and its evolution during homogenization were investigated by means of optical microscopy （OM）, scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDS）, X-ray diffraction （XRD）, and differential scanning calorimetry （DSC） analysis. The results indicate that the microstructure of the as-cast 7A55 aluminum alloy mainly consists of the dendritic network of aluminum solid solution, Al/AIZnMgCu eutectic phases, and intermetaUic compounds MgZn2, Al2CuMg, Al7Cu2Fe, and Al23CuFe4. After homogenization at 470℃ for 48 h, Al/AlZnMgCu eutectic phases are dissolved into the matrix, and a small amount of high melting-point secondary phases were formed, which results in an increasing of the starting melting temperature of 7A55 aluminum alloy The high melting-point secondary phases were eliminated mostly when the homogenization time achieved to 72 h. Therefore, the reasonable homogenization heat treatment process for 7A55 aluminum alloy ingots was chosen as 470℃/72 h.