ZnO/Cu/ZnO transparent conductive thin films were prepared by RF sputtering deposition of ZnO target and DC sputtering deposition of Cu target on n-type （001） Si and glass substrates at room temperature. The mor- ph...ZnO/Cu/ZnO transparent conductive thin films were prepared by RF sputtering deposition of ZnO target and DC sputtering deposition of Cu target on n-type （001） Si and glass substrates at room temperature. The mor- phology, structure, optical, and electrical properties of the multilayer films were characterized by field emission scanning electron microscope （FESEM）, X-ray diffraction （XRD）, UV/Vis spectrophotometer, and Hall effect mea- surement system. The influence of Cu layer thickness and the oxygen pressure in sputtering atmosphere on the film properties were studied. ZnO/Cu/ZnO transparent conduc- tive film fabricated in pure Ar atmosphere with 10 nm Cu layer thickness has the best performance： resistivity of 2.3 × 10^-4 Ω.cm, carrier concentration of 6.44 × 10^16 cm-2, mobility of 4.51 cm2.（V.s）-1, and acceptable aver- age transmittance of 80 % in the visible range. The trans- mittance and conductivity of the films fabricated with oxygen are lower than those of the films fabricated without oxygen, which indicates that oxygen atmosphere does not improve the optical and electrical properties of ZnO/Cu/ ZnO films.展开更多
基金financially supported by the National Nature Science Foundation of China (No. 21071098)the Project of International Cooperation of the Ministry of Science and Technology of China (No. 2011DFA50530)the Nanotechnology Program of Shanghai Science & Technology Committee (No. 12nm0504800)
文摘ZnO/Cu/ZnO transparent conductive thin films were prepared by RF sputtering deposition of ZnO target and DC sputtering deposition of Cu target on n-type （001） Si and glass substrates at room temperature. The mor- phology, structure, optical, and electrical properties of the multilayer films were characterized by field emission scanning electron microscope （FESEM）, X-ray diffraction （XRD）, UV/Vis spectrophotometer, and Hall effect mea- surement system. The influence of Cu layer thickness and the oxygen pressure in sputtering atmosphere on the film properties were studied. ZnO/Cu/ZnO transparent conduc- tive film fabricated in pure Ar atmosphere with 10 nm Cu layer thickness has the best performance： resistivity of 2.3 × 10^-4 Ω.cm, carrier concentration of 6.44 × 10^16 cm-2, mobility of 4.51 cm2.（V.s）-1, and acceptable aver- age transmittance of 80 % in the visible range. The trans- mittance and conductivity of the films fabricated with oxygen are lower than those of the films fabricated without oxygen, which indicates that oxygen atmosphere does not improve the optical and electrical properties of ZnO/Cu/ ZnO films.