For evaporation-deposited Ti films, face-centred cubic structure was observed at the initial stage of film growth, then transited to the hexagonal close-packed structure during film growing (less than 50 nm thick). Wh...For evaporation-deposited Ti films, face-centred cubic structure was observed at the initial stage of film growth, then transited to the hexagonal close-packed structure during film growing (less than 50 nm thick). While. for ion-beam sputter-deposited films. the structure of films always kept the fcc structure during all stages of film formation. The structure of film at initial growth stages relates with the substrate. It is discussed that different film processes and different growth stages provide different thermodynamic condition of film formation and result in the different crystal structures of films during the film formation展开更多
文摘For evaporation-deposited Ti films, face-centred cubic structure was observed at the initial stage of film growth, then transited to the hexagonal close-packed structure during film growing (less than 50 nm thick). While. for ion-beam sputter-deposited films. the structure of films always kept the fcc structure during all stages of film formation. The structure of film at initial growth stages relates with the substrate. It is discussed that different film processes and different growth stages provide different thermodynamic condition of film formation and result in the different crystal structures of films during the film formation