Polypyrrole/polyvinylalcohol（PPy/PVA） foam was prepared by direct foam polymerization in water and then it was coated on the indium-tin oxide transparent conductive glass（ITO） to form conventional three-electrode ...Polypyrrole/polyvinylalcohol（PPy/PVA） foam was prepared by direct foam polymerization in water and then it was coated on the indium-tin oxide transparent conductive glass（ITO） to form conventional three-electrode cell.FTIR and UV-vis spectra were adopted to characterize the molecular structure and the absorption spectra of foam material,respectively.The porous structure of PPy/PVA foams and their photoelectric conversion behaviors were studied.The dimension of the pores is bigger than 100μm in diameter.Compared with the smooth film,the V_（oc） and I_（sc） of the foam film enhanced by 1.58-fold and 5.59-fold,respectively.展开更多
基金supported by the National Natural Science Foundation of China(No.20773142,50533030)the National Research Fund for Fundamental Key Project(No.2006CB806200,2006CB932100 and 2007CB936403)863 project(No.2007AA032348 and 2008AA05Z308).
文摘Polypyrrole/polyvinylalcohol（PPy/PVA） foam was prepared by direct foam polymerization in water and then it was coated on the indium-tin oxide transparent conductive glass（ITO） to form conventional three-electrode cell.FTIR and UV-vis spectra were adopted to characterize the molecular structure and the absorption spectra of foam material,respectively.The porous structure of PPy/PVA foams and their photoelectric conversion behaviors were studied.The dimension of the pores is bigger than 100μm in diameter.Compared with the smooth film,the V_（oc） and I_（sc） of the foam film enhanced by 1.58-fold and 5.59-fold,respectively.