To enhance the thermoelectric effect of cement-based materials,conductive polyaniline(PANI)modified MnO_(2)powder was synthesized and used as a thermoelectric component in the cement composites.The nanostructured PANI...To enhance the thermoelectric effect of cement-based materials,conductive polyaniline(PANI)modified MnO_(2)powder was synthesized and used as a thermoelectric component in the cement composites.The nanostructured PANI was deposited on the surface of the nanorod-shapedα-MnO_(2)particle and the weight ratio of PANI to MnO_(2)was 22.3:77.7 in the composite.The synthesized PANI/MnO_(2)composite was nanostructured according to the SEM image.The test results of the thermoelectric properties proved that the PANI/MnO_(2)composite was effective as the Seebeck coefficient and electrical conductivity values of the cement composites with PANI/MnO_(2)inside were 3-4 orders of magnitude higher than those of pure cement paste and the thermal conductivity values of these cement samples were similar.The obtained maximum figure of merit(ZT)value(2.75×10^(-3))was much larger than that of conductive materials reinforced cement-based composites.The thermoelectric effect of cement composites is mainly enhanced by the increased Seebeck coefficient and electrical conductivity in this work.展开更多
基金Funded by the National Natural Science Foundation of China(Nos.51525903,51808369 and 52078247)the Natural Science Foundation of the Jiangsu Higher Education Institutions of China(No.20KJB560005)the Science Foundation of Nanjing Institute of Technology(No.YKJ201929)。
文摘To enhance the thermoelectric effect of cement-based materials,conductive polyaniline(PANI)modified MnO_(2)powder was synthesized and used as a thermoelectric component in the cement composites.The nanostructured PANI was deposited on the surface of the nanorod-shapedα-MnO_(2)particle and the weight ratio of PANI to MnO_(2)was 22.3:77.7 in the composite.The synthesized PANI/MnO_(2)composite was nanostructured according to the SEM image.The test results of the thermoelectric properties proved that the PANI/MnO_(2)composite was effective as the Seebeck coefficient and electrical conductivity values of the cement composites with PANI/MnO_(2)inside were 3-4 orders of magnitude higher than those of pure cement paste and the thermal conductivity values of these cement samples were similar.The obtained maximum figure of merit(ZT)value(2.75×10^(-3))was much larger than that of conductive materials reinforced cement-based composites.The thermoelectric effect of cement composites is mainly enhanced by the increased Seebeck coefficient and electrical conductivity in this work.