In this study,a novel iron-based catalyst system,Fe(acac)3/(isocyanoimino)triptenylphosphorane(IITP)/AlR3,was employed for the synthesis of syndiotactic 1,2-polybutadiene in hexane.This catalyst system exhibits remark...In this study,a novel iron-based catalyst system,Fe(acac)3/(isocyanoimino)triptenylphosphorane(IITP)/AlR3,was employed for the synthesis of syndiotactic 1,2-polybutadiene in hexane.This catalyst system exhibits remarkably high catalytic activity,achieving a polymerization activity of 762 kgpolymer·molcatalyst^(-1)·h^(-1)at 50℃with a[BD]/[Fe]molar ratio of 20000.Furthermore,living polymerization characteristic were observed during the investigation of the polymerization kinetics of 1,3-butadiene polymerization.These characteristics were well demonstrated by a narrow molecular weight distribution(PDI≈2.0)of the resulting polybutadiene and a linear relationship between-ln(1-c)and polymerization time as well as number average molecular weight and polymer yield.The resultant polymer showed a 1,2-selectivity of approximately 76%and stereoregularity ranging from 62%to 73%(rrrr).Additionally,through kinetic studies on polymerization reaction,an apparent activation energy Ea value of this catalytic system was calculated to be 84.98 kJ·mol^(-1),which suggests that high polymerization temperature favors efficient polymerization.展开更多
基金This work was financially supported by the National Key R&D Program of China(No.2022YFB3704700).
文摘In this study,a novel iron-based catalyst system,Fe(acac)3/(isocyanoimino)triptenylphosphorane(IITP)/AlR3,was employed for the synthesis of syndiotactic 1,2-polybutadiene in hexane.This catalyst system exhibits remarkably high catalytic activity,achieving a polymerization activity of 762 kgpolymer·molcatalyst^(-1)·h^(-1)at 50℃with a[BD]/[Fe]molar ratio of 20000.Furthermore,living polymerization characteristic were observed during the investigation of the polymerization kinetics of 1,3-butadiene polymerization.These characteristics were well demonstrated by a narrow molecular weight distribution(PDI≈2.0)of the resulting polybutadiene and a linear relationship between-ln(1-c)and polymerization time as well as number average molecular weight and polymer yield.The resultant polymer showed a 1,2-selectivity of approximately 76%and stereoregularity ranging from 62%to 73%(rrrr).Additionally,through kinetic studies on polymerization reaction,an apparent activation energy Ea value of this catalytic system was calculated to be 84.98 kJ·mol^(-1),which suggests that high polymerization temperature favors efficient polymerization.