Processing and properties of PcBN composites fabricated by HPHT using PSN and Al as sintering additive 被引量:5
1
作者 Ming-liang Li li-xing liang +4 位作者 Hai-Long Wang Peng-Bo Zhao Xiao-Tong Zhao Gang Shao Rui Zhang 《Rare Metals》 SCIE EI CAS CSCD 2020年第5期570-576,共7页
Dense polycrystalline cubic boron nitride(PcBN)composites were fabricated by high-pressure and high-temperature(HPHT)sintering using polysilazane(PSN)and Al as sintering additive.After high-energy ball milling,the cBN... Dense polycrystalline cubic boron nitride(PcBN)composites were fabricated by high-pressure and high-temperature(HPHT)sintering using polysilazane(PSN)and Al as sintering additive.After high-energy ball milling,the cBN fine particles were uniformly coated with PSN by ultrasonic treatment.After thermocuring and pyrolysis,the cBN–SiCN particles were mixed with Al The PcBN composites were prepared after sintering a1450°C for 10 min with a pressure of 5 GPa.The refining effect of high-energy ball milling on the c BN particles was studied by scanning electron microscopy(SEM)and laser particle size analyzer.The oxidation of the cBN particles after milling was investigated by nitrogen–oxygen analyzer.The phase composition and microstructure of the sintered PcBN composites were investigated by X-ray diffractometer(XRD)and SEM.The main phases of the sintered PcBN composites are c BN,AlN,SiC and Si3N4The conversion of cBN to hBN was inhibited by the formation of AlN.The mechanical properties of the sintered PcBN composites were improved by the appearance of SiC and Si3N4.The density and mechanical properties of the PcBN composites both increased with the content of the cBN particles increasing.The sintered sample with 60 wt%cBN,30 wt%PSN and 10 wt%Al showed the best results density of 99.7%,Vickers’hardness of(25.2±0.8)GPa and flexural strength of(602±15)MPa. 展开更多
关键词 Polycrystalline cubic boron nitride Highpressure and high-temperature sintering High-energy ball milling Mechanical properties
原文传递
上一页 1 下一页 到第
使用帮助 返回顶部