In this work,the BMS-12 pre-sintered material was used as the basic material,and the optimal secondary additive addition amount was found by the wet pressing process.Then,the anisotropic ferrite material was prepared ...In this work,the BMS-12 pre-sintered material was used as the basic material,and the optimal secondary additive addition amount was found by the wet pressing process.Then,the anisotropic ferrite material was prepared by dry-pres sing method,and the effects of camphor adhesives,calcium stearate lubricant and powder particle size on the magnetic properties were studied.The experimental results show that the appropriate addition amount of camphor adhesive and calcium stearate lubricant is 0.6 wt%and 0.8 wt%,respectively.High remanence and coercivity can be obtained for particle size of 0.85-1.00μm.Superior dry-pressed magnet ferrite was prepared with typical properties of magnetic induction intensity of Br=421 mT,induction coercivity of Hcb=296 kA·m-1,intrinsic coercivity of Hcj=369 kA·m-1 and maximum energy product of(BH)max=33.3 kJ·m-3,which have reached the level of TDK corporation product of FB5 D.This shows that the dry-pressed magnet of La-Ca-Sr-Co system has higher remanence and intrinsic coercivity than the traditional wetpressed Sr-ferrite.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51401023)the National Basic Research Program of China(No.2014CB643702)Youth Innovation Fund Project of BGRIMM Technology Group(Nos.QCJ201809,QC-201724 and QCJ201820).
文摘In this work,the BMS-12 pre-sintered material was used as the basic material,and the optimal secondary additive addition amount was found by the wet pressing process.Then,the anisotropic ferrite material was prepared by dry-pres sing method,and the effects of camphor adhesives,calcium stearate lubricant and powder particle size on the magnetic properties were studied.The experimental results show that the appropriate addition amount of camphor adhesive and calcium stearate lubricant is 0.6 wt%and 0.8 wt%,respectively.High remanence and coercivity can be obtained for particle size of 0.85-1.00μm.Superior dry-pressed magnet ferrite was prepared with typical properties of magnetic induction intensity of Br=421 mT,induction coercivity of Hcb=296 kA·m-1,intrinsic coercivity of Hcj=369 kA·m-1 and maximum energy product of(BH)max=33.3 kJ·m-3,which have reached the level of TDK corporation product of FB5 D.This shows that the dry-pressed magnet of La-Ca-Sr-Co system has higher remanence and intrinsic coercivity than the traditional wetpressed Sr-ferrite.