The sliding friction and wear behaviors of Mg-11Y-5Gd-2Zn-0.5Zr （wt%） alloy were investigated under oil lubricant condition by pin-on-disk configuration with a constant sliding distance of 1,000 m in the temperature...The sliding friction and wear behaviors of Mg-11Y-5Gd-2Zn-0.5Zr （wt%） alloy were investigated under oil lubricant condition by pin-on-disk configuration with a constant sliding distance of 1,000 m in the temperature range of 25-200℃. Results indicate that the volumetric wear rates and average friction coefficients decrease with the increase of sliding speeds, and increase with the increase of test temperature below 150℃. The hard and thermally stable Mg12（Y,Gd）Zn phase with long-period stacking order structure in the alloy presents significant wear resistance, The wear mechanism below 100℃ is abrasive wear as a result of plastic extrusion deformation. The corporate effects of severe abrasive, oxidative, and delaminating wear result in the tribological mechanism above 100℃.展开更多
A new Mg−10%Al−1%Zn−1%Si alloy with non-dendritic microstructure was prepared by strain induced melt activation(SIMA)process.The effect of compression ratio on the evolution of semisolid microstructure of the experime...A new Mg−10%Al−1%Zn−1%Si alloy with non-dendritic microstructure was prepared by strain induced melt activation(SIMA)process.The effect of compression ratio on the evolution of semisolid microstructure of the experimental alloy was investigated.The results indicate that the average size ofα-Mg grains decreases and spheroidizing tendency becomes more obvious with the compression ratios increasing from 0 to 40%.In addition,the eutectic Mg2Si phase in the Mg−10%Al−1%Zn−1%Si alloy transforms completely from the initial fishbone shape to globular shape by SIMA process.With the increasing of compression ratio,the morphology and average size of Mg2Si phases do not change obviously.The morphology modification mechanism of Mg2Si phase in Mg−10%Al−1%Zn−1%Si alloy by SIMA process was also studied.展开更多
基金supported by the National Natural Science Foundation of China (No. 51074106)Key HiTech Research and Development Program of China (No. 2009AA033501)National Key Technology R&D Program of China (No. 2011BAE22B01-5)
文摘The sliding friction and wear behaviors of Mg-11Y-5Gd-2Zn-0.5Zr （wt%） alloy were investigated under oil lubricant condition by pin-on-disk configuration with a constant sliding distance of 1,000 m in the temperature range of 25-200℃. Results indicate that the volumetric wear rates and average friction coefficients decrease with the increase of sliding speeds, and increase with the increase of test temperature below 150℃. The hard and thermally stable Mg12（Y,Gd）Zn phase with long-period stacking order structure in the alloy presents significant wear resistance, The wear mechanism below 100℃ is abrasive wear as a result of plastic extrusion deformation. The corporate effects of severe abrasive, oxidative, and delaminating wear result in the tribological mechanism above 100℃.
基金The authors are grateful for the financial supports from the National Natural Science Foundation of China(Nos.41807235,50674038).
文摘A new Mg−10%Al−1%Zn−1%Si alloy with non-dendritic microstructure was prepared by strain induced melt activation(SIMA)process.The effect of compression ratio on the evolution of semisolid microstructure of the experimental alloy was investigated.The results indicate that the average size ofα-Mg grains decreases and spheroidizing tendency becomes more obvious with the compression ratios increasing from 0 to 40%.In addition,the eutectic Mg2Si phase in the Mg−10%Al−1%Zn−1%Si alloy transforms completely from the initial fishbone shape to globular shape by SIMA process.With the increasing of compression ratio,the morphology and average size of Mg2Si phases do not change obviously.The morphology modification mechanism of Mg2Si phase in Mg−10%Al−1%Zn−1%Si alloy by SIMA process was also studied.