The microstructural, optical, and magnetic properties and room-temperature photoluminescence （PL） ofMn-doped ZnO thin films were studied. The chemical compositions were examined by energy dispersive X-ray spectrosco...The microstructural, optical, and magnetic properties and room-temperature photoluminescence （PL） ofMn-doped ZnO thin films were studied. The chemical compositions were examined by energy dispersive X-ray spectroscopy （EDS） and the charge state of Mn ions in the ZnO：Mn films was characterized by X-ray photoelectronic spectrometry （XPS）. From the X-ray diffraction （XRD） data of the samples, it can be found that Mn doping does not change the orientation of ZnO thin films. All the films prepared have a wurtzite structure and grow mainly along the c-axis orientation. The grain size and the residual stress were calculated from the XRD results. The optical transmittance of the film decreases with the increase of manganese content in ZnO. The room-temperature photoluminescence of the films shows that the in- tensity of near band energy （NBE） emission depends strongly on the Mn content. The hysteresis behavior indicates that the films with the Mn content below 9at% are ferromagnetic at room temperature.展开更多
基金supported by the National Natural Science Foundation of China(Nos.10774013,10974013,60978060,and 10804006)the National Natural Science Foundation of China for Distinguished Young Scholars(No.60825407)the Doctor Science Creative Grants of Beijing Jiaotong University(No.141028522)
文摘The microstructural, optical, and magnetic properties and room-temperature photoluminescence （PL） ofMn-doped ZnO thin films were studied. The chemical compositions were examined by energy dispersive X-ray spectroscopy （EDS） and the charge state of Mn ions in the ZnO：Mn films was characterized by X-ray photoelectronic spectrometry （XPS）. From the X-ray diffraction （XRD） data of the samples, it can be found that Mn doping does not change the orientation of ZnO thin films. All the films prepared have a wurtzite structure and grow mainly along the c-axis orientation. The grain size and the residual stress were calculated from the XRD results. The optical transmittance of the film decreases with the increase of manganese content in ZnO. The room-temperature photoluminescence of the films shows that the in- tensity of near band energy （NBE） emission depends strongly on the Mn content. The hysteresis behavior indicates that the films with the Mn content below 9at% are ferromagnetic at room temperature.