The hot corrosion behavior of Ti45 A18.5 Nb alloy was studied in the salt of Na_(2)SO_(4)and/or NaCl at 700℃.To improve the hot corrosion resistance,Ti45 A18.5 Nb alloy was anodized in fluorine-containing solution an...The hot corrosion behavior of Ti45 A18.5 Nb alloy was studied in the salt of Na_(2)SO_(4)and/or NaCl at 700℃.To improve the hot corrosion resistance,Ti45 A18.5 Nb alloy was anodized in fluorine-containing solution and pre-oxidized in air.Results showed that the combination of anodization and pre-oxidation can efficiently enhance the hot corrosion resistance of Ti45 A18.5 Nb alloy contaminated with Na_(2)SO_(4)or Na_(2)SO_(4)+NaCl deposits.This is because anodization and pre-oxidation result in the formation of compact AlOlayer which can act as a diffusion barrier to prevent sulfur,chlorine,and oxygen from attacking the alloy,therefore providing good resistance against hot corrosion.When exposed to NaCl deposit,however,no obvious improvement was achieved on the hot corrosion behavior no matter the alloy was anodized or further pre-oxidized in air.展开更多
基金financially supported by the National Natural Science Foundation of China(Nos.52071347,51971205)the Innovation Group Project of Southern Marine Science and Engineering Guangdong Laboratory(Zhuhai),China(No.311020012)。
基金The authors are grateful for the financial supports from the National Natural Science Foundation of China(51971205)Shenzhen Science and Technology Innovation Program,China(JCYJ20190807154005593)the Fundamental Research Funds for the Central Universities,China(19lgpy20).
基金financial supports from the National Natural Science Foundation of China (No. 51971205)the Guangdong Basic and Applied Basic Research Foundation, China (No. 2021B1515020056)the Shenzhen Fundamental Research Program, China (No. JCYJ20190807154005593)。
基金supported by the National Natural Science Foundation of China(No.51971205)the Guangdong Basic and Applied Basic Research Foundation(No.2021B1515020056)the Basic Research Project of Shenzhen Science and Technology Innovation Program(No.JCYJ20190807154005593)。
文摘The hot corrosion behavior of Ti45 A18.5 Nb alloy was studied in the salt of Na_(2)SO_(4)and/or NaCl at 700℃.To improve the hot corrosion resistance,Ti45 A18.5 Nb alloy was anodized in fluorine-containing solution and pre-oxidized in air.Results showed that the combination of anodization and pre-oxidation can efficiently enhance the hot corrosion resistance of Ti45 A18.5 Nb alloy contaminated with Na_(2)SO_(4)or Na_(2)SO_(4)+NaCl deposits.This is because anodization and pre-oxidation result in the formation of compact AlOlayer which can act as a diffusion barrier to prevent sulfur,chlorine,and oxygen from attacking the alloy,therefore providing good resistance against hot corrosion.When exposed to NaCl deposit,however,no obvious improvement was achieved on the hot corrosion behavior no matter the alloy was anodized or further pre-oxidized in air.