The microstructure and properties of the as-cast,as-homogenized and as-extruded Mg−6Zn−4Sn−1Mn(ZTM641)alloy with various Al contents(0,0.5,1,2,3 and 4 wt.%)were investigated by OM,XRD,DSC,SEM,TEM and uniaxial tensile ...The microstructure and properties of the as-cast,as-homogenized and as-extruded Mg−6Zn−4Sn−1Mn(ZTM641)alloy with various Al contents(0,0.5,1,2,3 and 4 wt.%)were investigated by OM,XRD,DSC,SEM,TEM and uniaxial tensile tests.The results show that when the Al content is not higher than 0.5%,the alloys are mainly composed of α-Mg,Mg_(2)Sn,Al_(8)Mn_(5)and Mg_(7)Zn_(3)phases.When the Al content is higher than 0.5%,the alloys mainly consist ofα-Mg,Mg_(2)Sn,MgZn,Mg_(32)(Al,Zn)_(49),Al_(2)Mg_(5)Zn_(2),Al_(11)Mn_(4)and Al_(8)Mn_(5)phases.A small amount of Al(≤1%)can increase the proportion of fine dynamic recrystallized(DRXed)grains during hot-extrusion process.The roomtemperature tensile test results show that the ZTM641−1Al alloy has the best comprehensive mechanical properties,in which the ultimate tensile strength is 332 MPa,yield strength is 221 MPa and the elongation is 15%.Elevatedtemperature tensile test results at 150 and 200℃ show that ZTM641−2Al alloy has the best comprehensive mechanical properties.展开更多
基金the financial supports from the National Natural Science Foundation of China(No.51701172)Educational Commission of Hunan Province,China(No.20B579)+2 种基金Major Program of Hunan Province,China(No.2018RS3091)China Postdoctoral Science Foundation(No.2018M632977)the Natural Science Foundation of Hunan Province,China(No.2018JJ3504).
文摘The microstructure and properties of the as-cast,as-homogenized and as-extruded Mg−6Zn−4Sn−1Mn(ZTM641)alloy with various Al contents(0,0.5,1,2,3 and 4 wt.%)were investigated by OM,XRD,DSC,SEM,TEM and uniaxial tensile tests.The results show that when the Al content is not higher than 0.5%,the alloys are mainly composed of α-Mg,Mg_(2)Sn,Al_(8)Mn_(5)and Mg_(7)Zn_(3)phases.When the Al content is higher than 0.5%,the alloys mainly consist ofα-Mg,Mg_(2)Sn,MgZn,Mg_(32)(Al,Zn)_(49),Al_(2)Mg_(5)Zn_(2),Al_(11)Mn_(4)and Al_(8)Mn_(5)phases.A small amount of Al(≤1%)can increase the proportion of fine dynamic recrystallized(DRXed)grains during hot-extrusion process.The roomtemperature tensile test results show that the ZTM641−1Al alloy has the best comprehensive mechanical properties,in which the ultimate tensile strength is 332 MPa,yield strength is 221 MPa and the elongation is 15%.Elevatedtemperature tensile test results at 150 and 200℃ show that ZTM641−2Al alloy has the best comprehensive mechanical properties.