This study aimed to assess the differences of characteristics between the new ferronickel slag generated from the production of nickel and the slag which had been used as a material reclamation. The Toxicity Character...This study aimed to assess the differences of characteristics between the new ferronickel slag generated from the production of nickel and the slag which had been used as a material reclamation. The Toxicity Characteristic Leaching Procedure (TCLP) test was conducted on ferronickel slag to determine the concentration of heavy metals leaching. Then, the tests of X-Ray Diffraction (XRD), Scanning Electron Microscopic (SEM) and Energy-Dispersive X-Ray Spectroscopy (EDX) are also conducted on the ferronickel slag samples. The results of TCLP test show that the new ferronickel slag samples contain Fe (158, 6775 ppm), Cr (0.64465 ppm), and Pb (0.0219 ppm), and that the ferronickel slag has been used as a reclamation material containing Fe (3.94 ppm) and Cr (2.91 ppm). The result of EDX test shows that the slag sample from the reclamation area contains higher Ni concentration than the new slag sample. Slag that has been used for reclamation contains high SiO2 and Mg2(SiO6). The XRD analysis result shows that the highest elements in the slag are Si and Mg with 18.94% and 15.83% respectively. The dominant mineral in the slag is forsterite (Mg 1.784 FeSiO4 0216) by 41% and the rest is magnesium silicate (Mg2(SiO6)).展开更多
文摘This study aimed to assess the differences of characteristics between the new ferronickel slag generated from the production of nickel and the slag which had been used as a material reclamation. The Toxicity Characteristic Leaching Procedure (TCLP) test was conducted on ferronickel slag to determine the concentration of heavy metals leaching. Then, the tests of X-Ray Diffraction (XRD), Scanning Electron Microscopic (SEM) and Energy-Dispersive X-Ray Spectroscopy (EDX) are also conducted on the ferronickel slag samples. The results of TCLP test show that the new ferronickel slag samples contain Fe (158, 6775 ppm), Cr (0.64465 ppm), and Pb (0.0219 ppm), and that the ferronickel slag has been used as a reclamation material containing Fe (3.94 ppm) and Cr (2.91 ppm). The result of EDX test shows that the slag sample from the reclamation area contains higher Ni concentration than the new slag sample. Slag that has been used for reclamation contains high SiO2 and Mg2(SiO6). The XRD analysis result shows that the highest elements in the slag are Si and Mg with 18.94% and 15.83% respectively. The dominant mineral in the slag is forsterite (Mg 1.784 FeSiO4 0216) by 41% and the rest is magnesium silicate (Mg2(SiO6)).