An innovative joint interface design for reducing intermetallic compounds and improving joint strength of thick plate friction stir welded Al/Mg joints

Friction stir welding of dissimilar Al/Mg thick plates still faces severe challenges, such as poor formability, formation of thick intermetallic compounds, and low joint strength. In this work, two joint configurations, namely inclined butt(conventional butt) and serrated interlocking(innovative butt), are proposed for improving weld formation and joint quality. The results show that a continuous and straight intermetallic compound layer appears at the Mg side interface in conventional butt joint, and the maximum average thickness reaches about 60.1 μm.Additionally, the Mg side interface also partially melts, forming a eutectic structure composed of Mg solid solution and Al_(12)Mg_(17) phase.For the innovative butt joint, the Mg side interface presents the curved interlocking feature, and intermetallic compounds can be reduced to less than 10 μm. The joint strength of innovative butt joint is more than three times that of conventional butt joint. This is due to the interlocking effect and thin intermetallic compounds in the innovative joint.

Repairing of exit-hole in friction-stir-spot welded joints for 2024-T4 aluminum alloy by resistance welding

The exit-hole in friction stir spot welded(FSSWed) 2024-T4 aluminum alloy joints was successfully repaired by using a three-phase secondary rectification resistance spot welding machine, which is termed as filling exit-hole based on resistance welding(FEBRW). The filling dynamic behavior of force was recorded by a device monitoring. Optical microscope(OM), electron backscatter diffraction(EBSD), and tensile shear tests and finite element modelling were conducted to investigate the repairing stages and bonding mechanisms of the repaired joints in detail. Results showed that exit-hole was completely filled and repaired experiencing three stages. Metallurgical bonding was achieved between plug and exit-hole wall in two forms, including melting bonding in the middle of the joints and partial diffusion bonding on both the upper and bottom of the joints. The highest tensile shear strength of the repaired joints was 7.43 kN, which was 36.3% higher than that of the as welded joints. Resistance welding paves an efficient way to repair the exit-hole in FSSWed joints.

Improving tensile-shear properties of friction stir lap welded dissimilar Al/Mg joints by eliminating hook defect and controlling interfacial reaction

To improve tensile-shear properties of fiction stir lap welded(FSLW) dissimilar Al/Mg joints, pin-tip profiles were innovatively designed and welding speed was optimized, and effects of them on formation, interface microstructure and mechanical properties of different FSLW joints were investigated. With increasing the welding speed, the tensile-shear load of FSLW joints produced by three pins presents an increasing firstly and then decreasing trend. Compared with Rpin, the hook and hole defect in the joints made by S-pin and T-pin are eliminated owing to additional eccentric force. Moreover, the joints obtained by T-pin at 75 mm/min have the highest tensile-shear load, and a maximum value of 3.425 kN is produced, which increases by 96.8%.Meanwhile, the pin-tip profile improves significantly the interface reaction depending on the welding temperature. For R-pin, thick brittle intermetallic compounds of about 6.9 μm Al3Mg2and 13.3 μm Al12Mg17layers at the welding interface derived from diffusion reaction are formed, resulting in continuous cracks. However, using T-pin can raise the interface temperature, and which makes the interface liquefy locally to generate only 2.2 μm Al3Mg2layer and dispersive(Al12-Mg17+Mg) eutectic structure. This can release high residual stress and remove welding crack, consequently enhancing the interface properties of T-pin joints.

Inhomogeneity of microstructure and mechanical properties in the nugget of friction stir welded thick 7075 aluminum alloy joints

In this study, 20 mm thick AA7075-T6 alloy plates were joined by friction stir welding. The microstructure and mechanical properties of the nugget zone along the thickness direction from the top to the bottom was investigated. The results showed that the microstructure including the grain size, the degree of dynamic recrystallization, the misorientation angle distribution and the precipitation phase containing its size, type and content exhibited a gradient distribution along the thickness direction. The testing results of mechanical properties of the slices showed that the nugget was gradually weakened along the depth from the top to the bottom. The maximum ultimate tensile strength, yield strength and elongation of the slice in the nugget top-middle are obtained, which are 415 MPa, 255 MPa and 8.1%, respectively.