Non-spherical Cu@Cu S yolk–shell structures are successfully obtained using Cu_2 O cube templates in a process combining rapid surface sulfidation followed by disproportionation of the Cu_2 O core upon treatment with...Non-spherical Cu@Cu S yolk–shell structures are successfully obtained using Cu_2 O cube templates in a process combining rapid surface sulfidation followed by disproportionation of the Cu_2 O core upon treatment with a hydrochloric acid solution. By employing the above method,Cu@Cu S yolk–shell structures with different morphologies,including octahedral, truncated octahedral, and cuboctahedral shapes, can be synthesized. The void space within the hollow structures provides a unique confined space, where the metallic copper present in the core of a shell can be protected from agglomeration and oxidation. Furthermore,the presence of metal copper in these hollow structurescontributes to improvement in the photocatalytic properties of these materials. The application of these Cu@Cu S structures indeed shows clearly improved photocatalytic performance.展开更多
基金supported by the National Natural Science Foundation of China (Grant Nos. 21671085, 21473081, 21201088)the Natural Science Foundation of Jiangsu Province (BK20161160)the Qing Lan Project and the Project Funded by the Priority Academic Program Development of Jiangsu Higher Education Institutions
文摘Non-spherical Cu@Cu S yolk–shell structures are successfully obtained using Cu_2 O cube templates in a process combining rapid surface sulfidation followed by disproportionation of the Cu_2 O core upon treatment with a hydrochloric acid solution. By employing the above method,Cu@Cu S yolk–shell structures with different morphologies,including octahedral, truncated octahedral, and cuboctahedral shapes, can be synthesized. The void space within the hollow structures provides a unique confined space, where the metallic copper present in the core of a shell can be protected from agglomeration and oxidation. Furthermore,the presence of metal copper in these hollow structurescontributes to improvement in the photocatalytic properties of these materials. The application of these Cu@Cu S structures indeed shows clearly improved photocatalytic performance.