In this work,a surfactant,benzalkonium chloride(BAC),was used to study its effects on both the growth of Chlorella vulgaris and the corrosion caused by its biofilm.Experimental results indicated that BAC at a low conc...In this work,a surfactant,benzalkonium chloride(BAC),was used to study its effects on both the growth of Chlorella vulgaris and the corrosion caused by its biofilm.Experimental results indicated that BAC at a low concentration of 3 mg/L suppressed C.vulgaris growth and achieved 81%corrosion inhibition based on weight loss reduction.The inhibition effects increased when the BAC dosage was increased.At 30 mg/L,the corrosion inhibition increased to 95%.Electrochemical results supported surface pitting analysis,weight loss results data and confirmed the corrosion inhibition.展开更多
基金supported by National Key Research and Development Program of China(2018YFF0215002)Graduates’Innovation Fund of Huazhong University of Science and Technology(5003013044)+2 种基金The Open Fund of Hubei Key Laboratory of Materials Chemistry and Service Failure(2017)Key Laboratory of Materials Chemistry for Energy Conversion and Storage,Ministry of Education(2018)Natural Science Foundation of the Jiangsu Higher Education Institutions of China(No.18KJB530004)。
文摘In this work,a surfactant,benzalkonium chloride(BAC),was used to study its effects on both the growth of Chlorella vulgaris and the corrosion caused by its biofilm.Experimental results indicated that BAC at a low concentration of 3 mg/L suppressed C.vulgaris growth and achieved 81%corrosion inhibition based on weight loss reduction.The inhibition effects increased when the BAC dosage was increased.At 30 mg/L,the corrosion inhibition increased to 95%.Electrochemical results supported surface pitting analysis,weight loss results data and confirmed the corrosion inhibition.