A novel porous binder was obtained from acid-treated kaolin. This new binder possessed abundant meso/macropores, good hydrothermal stability and heavy metal resistance. The prepared catalyst using new binder featured ...A novel porous binder was obtained from acid-treated kaolin. This new binder possessed abundant meso/macropores, good hydrothermal stability and heavy metal resistance. The prepared catalyst using new binder featured low attrition index and large pore volume. The catalysts were contaminated with Ni, V, and tested in a fixed-fluidized bed reactor unit. In comparison with the reference sample, the oil conversion achieved by the above-mentioned catalyst increased by 3.50 percentage points, and heavy oil yield decreased by 2.86 percentage points, while the total liquid yield and light oil yield increased by 2.82 percentage points and 0.79 percentage points, respectively. The perfect pore structure, good hydrothermal stability and heavy metal resistant performance of new binder were the possible causes leading to its outstanding performance.展开更多
A new silica sol binder was obtained by mixing the acid-modified aluminium sulfate and water glass. The effect of SiO2 concentration in sodium silicate, pH value and polymerization was investigated. The new silica sol...A new silica sol binder was obtained by mixing the acid-modified aluminium sulfate and water glass. The effect of SiO2 concentration in sodium silicate, pH value and polymerization was investigated. The new silica sol binder, which possessed abundant pore volume and suitable acid amount, was an ideal component for preparing cracking catalyst. As a result, the corresponding catalyst comprising the new binder showed excellent performance. Compared with the reference sample, the liquefied petroleum gas(LPG) and propylene yield obtained over this catalyst increased by 3.49 and 1.20 percentage points, respectively. The perfect pore structure and suitable Lewis acid amount of new silica sol were the possible reason leading to its outstanding performance.展开更多
基金the Department of Science and Technology Management of PetroChina for providing financial support
文摘A novel porous binder was obtained from acid-treated kaolin. This new binder possessed abundant meso/macropores, good hydrothermal stability and heavy metal resistance. The prepared catalyst using new binder featured low attrition index and large pore volume. The catalysts were contaminated with Ni, V, and tested in a fixed-fluidized bed reactor unit. In comparison with the reference sample, the oil conversion achieved by the above-mentioned catalyst increased by 3.50 percentage points, and heavy oil yield decreased by 2.86 percentage points, while the total liquid yield and light oil yield increased by 2.82 percentage points and 0.79 percentage points, respectively. The perfect pore structure, good hydrothermal stability and heavy metal resistant performance of new binder were the possible causes leading to its outstanding performance.
基金the Department of Science and Technology Management of PetroChina for providing financial support
文摘A new silica sol binder was obtained by mixing the acid-modified aluminium sulfate and water glass. The effect of SiO2 concentration in sodium silicate, pH value and polymerization was investigated. The new silica sol binder, which possessed abundant pore volume and suitable acid amount, was an ideal component for preparing cracking catalyst. As a result, the corresponding catalyst comprising the new binder showed excellent performance. Compared with the reference sample, the liquefied petroleum gas(LPG) and propylene yield obtained over this catalyst increased by 3.49 and 1.20 percentage points, respectively. The perfect pore structure and suitable Lewis acid amount of new silica sol were the possible reason leading to its outstanding performance.