A series of new(Al_(18)Co_(13)Cr_(10)Fe_(14)Ni_(45))(100−x)Tix(x=0,0.5,1)eutectic high-entropy alloys(EHEAs)were designed and prepared with the aid of empirical parameter calculations and JMatPro software predictions....A series of new(Al_(18)Co_(13)Cr_(10)Fe_(14)Ni_(45))(100−x)Tix(x=0,0.5,1)eutectic high-entropy alloys(EHEAs)were designed and prepared with the aid of empirical parameter calculations and JMatPro software predictions.The effects of Ti addition on the microstructures,phase structures,and mechanical properties of Al_(18)Co_(13)Cr_(10)Fe_(14)Ni_(45) EHEA were investigated.The results show that(Al_(18)Co_(13)Cr_(10)Fe_(14)Ni_(45))_((100−x))Ti_(x)(x=0,0.5,1)EHEAs are composed of the FCC and B2 phases.With the increase in Ti content,the strength of the EHEAs increases.The volume fraction of the FCC phase decreases,and the volume fraction of B2 phase increases;the size of nanoprecipitates within the B2 phase decreases and the number of them increases,which could be responsible for the high strength due to the addition of Ti.Among them,(Al_(18)Co_(13)Cr_(10)Fe_(14)Ni_(45))99.5Ti0.5 alloy exhibited excellent properties with yield strength,ultimate tensile strength,and ductility of 690 MPa,1065 MPa,and 9.18%,respectively.展开更多
基金This work was supported by the National Natural Science Foundation of China(Nos.52001051 and U20A20278)the National Key Research and Development Program of China(Nos.2018YFA0702901 and 2019YFA0209901)+1 种基金the Liao Ning Revitalization Talents Program(No.XLYC1807047)the Major Special Project of“Scientific and Technological Innovation 2025”in Ningbo(No.2019B10086).
文摘A series of new(Al_(18)Co_(13)Cr_(10)Fe_(14)Ni_(45))(100−x)Tix(x=0,0.5,1)eutectic high-entropy alloys(EHEAs)were designed and prepared with the aid of empirical parameter calculations and JMatPro software predictions.The effects of Ti addition on the microstructures,phase structures,and mechanical properties of Al_(18)Co_(13)Cr_(10)Fe_(14)Ni_(45) EHEA were investigated.The results show that(Al_(18)Co_(13)Cr_(10)Fe_(14)Ni_(45))_((100−x))Ti_(x)(x=0,0.5,1)EHEAs are composed of the FCC and B2 phases.With the increase in Ti content,the strength of the EHEAs increases.The volume fraction of the FCC phase decreases,and the volume fraction of B2 phase increases;the size of nanoprecipitates within the B2 phase decreases and the number of them increases,which could be responsible for the high strength due to the addition of Ti.Among them,(Al_(18)Co_(13)Cr_(10)Fe_(14)Ni_(45))99.5Ti0.5 alloy exhibited excellent properties with yield strength,ultimate tensile strength,and ductility of 690 MPa,1065 MPa,and 9.18%,respectively.