EFFECTS OF WAVEFORM AND FREQUENCY OF CYCLIC LOADING ON CORROSION FATIGUE CRACK PROPAGATION FOR GC－4 STEEL IN 3．5％NaCl SOLUTION

Abstract Experimental investigations were carried out of the effects of waveforms includingtriangular, positive sawtooth,negative sawtooth,square and negative Pulse) and frequen-cics including l,5 and 20Hz) of cyclic loading on the fatigue crack propagation fFCPj forGC-4 (40CrMnSiMoVA) steel in neutral 3.5% NaCI solution.Test results show thatwaveform and frequency have great effect on FCP rates of GC4 steel in 3.5% NaCl solution.Moreover,test results also show that the static stress corrosion cracking(SSCC)anddynamic stress corrosion cracking (DSCC) can occur simultaneously in the corrosion fatigue ICF) process and that the DSCC may be able to occur at K(max)<KISCC.Based on theexperimental results and the analysis in this study,a modified process competition modelwas presumably proposed, which can reasonably explain the test results obtained in thisstudy.

Inconel 718合金在高酸性石油井下工具服役环境中的应力腐蚀开裂行为

利用高温高压釜和有限元技术研究了Inconel 718合金在150℃、3.5 MPa H2S分压、3.5 MPa CO_2分压、含100 g/L Cl^-水溶液中的SCC敏感性。结果表明:在模拟高温高酸性工况下,未发现Inconel 718合金发生点蚀和应力腐蚀开裂。拉扭复合载荷对Inconel 718合金耐蚀性的影响体现在拉扭复合载荷作用下材料产生的Von Mises等效应力对其耐蚀性的影响。

高压直流干扰下X80钢在广东土壤中的干扰参数变化规律及腐蚀行为研究

通过室内模拟实验考察了大幅高压直流干扰电压下,X80钢在广东土壤中的干扰电流密度变化规律及腐蚀行为。结果表明,在50~300 V直流干扰电压下,电流密度随时间的变化呈现典型的3阶段特征:首先,在几秒内急剧上升到较高水平的峰值;然后,在几百秒内下降到较低水平的稳定值;最后,较长时间内维持在稳定值水平。结合干扰过程中试样附近土壤温度、含水率及电阻的测试分析表明,电流密度变化主要是由大幅干扰电压造成短时间内试片周围土壤温度升高,含水率降低,局部电阻率大幅增加所致。同时实验获得直流干扰电压分别为50、100、200及300 V时,1 h干扰实验中X80钢腐蚀速率分别为5.56、7.85、10.63及7.78 mm/h;腐蚀速率随直流干扰电压的升高呈现先增大后减小的趋势,该趋势不同于电流密度峰值随直流干扰电压的变化规律,但与电流密度稳定值的变化规律相似。此外,分析了高压直流干扰下试样腐蚀速率与使用3种形式电流密度计算得到的理论腐蚀速率之间的相关性。结果表明,利用干扰过程中电流密度曲线积分计算得出的理论腐蚀速率误差最小;利用电流密度稳定值计算得到的腐蚀速率误差次之;利用电流密度峰值计算得出的理论腐蚀速率误差最大,可达到实测腐蚀速率的若干倍。据此提出了实际高压直流干扰下参数监测与腐蚀速率的预测方法。

轨道交通对埋地管道动态直流干扰腐蚀的研究进展

分别从动态直流杂散电流干扰的腐蚀规律、机理研究以及腐蚀评判标准方面,介绍了国内外轨道交通对埋地管道动态直流杂散电流干扰的研究现状和进展,并对动态直流杂散电流干扰腐蚀的相关研究方向提出展望。