In the present work, the glass formation of Zr59Nb5Cu18Ni8Al10 (numbers indicate at %) alloy with diameter of 2 mm was prepared through water-cooled copper mold casting and in a ribbon form by the single roller melt-s...In the present work, the glass formation of Zr59Nb5Cu18Ni8Al10 (numbers indicate at %) alloy with diameter of 2 mm was prepared through water-cooled copper mold casting and in a ribbon form by the single roller melt-spinning method. This study is primarily devoted to evaluating the results obtained with the two methods of the development. The thermal stability was evaluated by differential scanning calorimetry (DSC) at a heating rate of 10℃/mn. The characteristic data of the bulk metallic glass are presented, including glass transition temperature (Tg) and crystallization temperature (Tx). The microstructure and constituent phases of the alloy composite have been analyzed by using X-ray diffraction, and observed by Scanning Electron Microscopy (SEM). The mechanical properties of bulk Zr59Nb5Cu18Ni8Al10 were alloy measured by compression tests at room temperature.展开更多
Fe-based bulk metallic glasses (BMGs) have been extensively studied due to their potential technological applications and their interesting physical properties such as a low modulus of elasticity, high yielding stress...Fe-based bulk metallic glasses (BMGs) have been extensively studied due to their potential technological applications and their interesting physical properties such as a low modulus of elasticity, high yielding stress and good magnetic properties. In the present work, the bulk metallic glass (BMG) formation of Fe40Ni40B20 (numbers indicate at %) with a ribbon form was fabricated by the single roller melt-spinning method. Rapid solidification leads to a fully amorphous structure for all compositions. The thermal properties associated with crystallization temperature of the glassy samples were measured using differential scanning calorimetry (DSC) at a heating rate of 10℃/mn. The microstructure and constituent phase of the alloy composite have been analyzed by using X-ray diffractometry (XRD). The effect of high temperature on the isothermal crystallization of Fe40Ni40B20 ribbon was investigated by HTX-ray diffraction. In addition, these ribbon glasses also exhibit good soft magnetic properties with M-H curvature measured under the magnetic fields between –1 kOe and 1 kOe.展开更多
文摘In the present work, the glass formation of Zr59Nb5Cu18Ni8Al10 (numbers indicate at %) alloy with diameter of 2 mm was prepared through water-cooled copper mold casting and in a ribbon form by the single roller melt-spinning method. This study is primarily devoted to evaluating the results obtained with the two methods of the development. The thermal stability was evaluated by differential scanning calorimetry (DSC) at a heating rate of 10℃/mn. The characteristic data of the bulk metallic glass are presented, including glass transition temperature (Tg) and crystallization temperature (Tx). The microstructure and constituent phases of the alloy composite have been analyzed by using X-ray diffraction, and observed by Scanning Electron Microscopy (SEM). The mechanical properties of bulk Zr59Nb5Cu18Ni8Al10 were alloy measured by compression tests at room temperature.
文摘Fe-based bulk metallic glasses (BMGs) have been extensively studied due to their potential technological applications and their interesting physical properties such as a low modulus of elasticity, high yielding stress and good magnetic properties. In the present work, the bulk metallic glass (BMG) formation of Fe40Ni40B20 (numbers indicate at %) with a ribbon form was fabricated by the single roller melt-spinning method. Rapid solidification leads to a fully amorphous structure for all compositions. The thermal properties associated with crystallization temperature of the glassy samples were measured using differential scanning calorimetry (DSC) at a heating rate of 10℃/mn. The microstructure and constituent phase of the alloy composite have been analyzed by using X-ray diffractometry (XRD). The effect of high temperature on the isothermal crystallization of Fe40Ni40B20 ribbon was investigated by HTX-ray diffraction. In addition, these ribbon glasses also exhibit good soft magnetic properties with M-H curvature measured under the magnetic fields between –1 kOe and 1 kOe.