Studies of Structure, Microstructure and Magnetic Properties of Fe70Si20Cr10 Nanocrystalline Alloy
1
作者 N. Ammouchi Z. Bensebaa +3 位作者 A. Otmani A. Dj ekoun m. bououdina J. m. Greneche 《Journal of Physical Science and Application》 2016年第1期9-9,共1页
Nanostructured Fe70Si20Cr10 alloy was produced by high energy planetary ball milling, starting from elemental powders. The structural, microstructural and magnetic properties of the milled powders were characterized b... Nanostructured Fe70Si20Cr10 alloy was produced by high energy planetary ball milling, starting from elemental powders. The structural, microstructural and magnetic properties of the milled powders were characterized by X-ray diffraction, scanning electron microscopy, vibrating sample magnetometer and 57Fe M6ssbauer. After 5 h of milling, it is observed the formation of a bcc solid solutions ~t-Fe (Si, Cr). Its grain size decreases with increasing milling time attaining 20 nm after 15 h of milling time. Analysis of M6ssbauer spectra shows an increasing broad magnetic component when the milling time increases. Its mean hyperfme field is about 25.5 T at 15 h of milling. M-H hysteresis loop curves reveal a room temperature ferromagnetic behaviour with a saturation magnetisation reaching 143 emu/g after 15 hours of milling, which is 20% lower than that of bulk iron; i.e., 1800 emu/g, due to effect of alloying elements after the formation of ct-Fe (Si, Cr) solid solution. 展开更多
关键词 Nanocrystalline material mechanical alloying X-rays diffraction 57Fe Mossbauer spectrometry magnetic properties.
下载PDF
上一页 1 下一页 到第
使用帮助 返回顶部