The effect of Ca addition on modification of primary Mg_(2)Si,hardness and wear behavior in Mg-5 wt.%Si hypereutectic alloy has been investigated.The results showed clearly that without Ca addition,most of primary Mg_...The effect of Ca addition on modification of primary Mg_(2)Si,hardness and wear behavior in Mg-5 wt.%Si hypereutectic alloy has been investigated.The results showed clearly that without Ca addition,most of primary Mg_(2)Si appeared as coarse dendritic morphology with average size of about 215μm.With the addition of 0.1 wt.%Ca,the average size of primary Mg_(2)Si decreased to about 98μm,but their morphologies did not significantly changed.As the addition level of Ca increased to 0.3 wt.%,the average size of primary Mg_(2)Si decreased significantly to about 50μm and their morphologies changed to polyhedral shape.However,with further increasing Ca addition to 0.6 wt.%and 1 wt.%,some needle-like and blocky CaMgSi particles formed and the average size of primary Mg_(2)Si increased slightly,which could described as over-modification.The present work showed that the optimal modification effect could be obtained when the Ca content in the investigated alloy reached 0.3 wt.%.The modification mechanism may be referred mainly due to poisoning effect resulting from the segregation of Ca atoms at the growth front of the Mg_(2)Si and the adsorption effect of some Ca atoms in the Mg_(2)Si crystal growth plane.The 0.3 wt.%Ca-added alloy has the highest hardness value and the best wear resistance among all other alloys.An excessive Ca addition resulted in the formation of some needle-like and blocky CaMgSi particles,which was detrimental to hardness and wear behavior of the 0.6 wt.%and 1 wt.%Ca-added alloys.The wear mechanism of investigated alloys is a mild abrasive oxidative wear with little adhesion.展开更多
文摘The effect of Ca addition on modification of primary Mg_(2)Si,hardness and wear behavior in Mg-5 wt.%Si hypereutectic alloy has been investigated.The results showed clearly that without Ca addition,most of primary Mg_(2)Si appeared as coarse dendritic morphology with average size of about 215μm.With the addition of 0.1 wt.%Ca,the average size of primary Mg_(2)Si decreased to about 98μm,but their morphologies did not significantly changed.As the addition level of Ca increased to 0.3 wt.%,the average size of primary Mg_(2)Si decreased significantly to about 50μm and their morphologies changed to polyhedral shape.However,with further increasing Ca addition to 0.6 wt.%and 1 wt.%,some needle-like and blocky CaMgSi particles formed and the average size of primary Mg_(2)Si increased slightly,which could described as over-modification.The present work showed that the optimal modification effect could be obtained when the Ca content in the investigated alloy reached 0.3 wt.%.The modification mechanism may be referred mainly due to poisoning effect resulting from the segregation of Ca atoms at the growth front of the Mg_(2)Si and the adsorption effect of some Ca atoms in the Mg_(2)Si crystal growth plane.The 0.3 wt.%Ca-added alloy has the highest hardness value and the best wear resistance among all other alloys.An excessive Ca addition resulted in the formation of some needle-like and blocky CaMgSi particles,which was detrimental to hardness and wear behavior of the 0.6 wt.%and 1 wt.%Ca-added alloys.The wear mechanism of investigated alloys is a mild abrasive oxidative wear with little adhesion.