Cu-Ni alloy nanoparticles were prepared by a microwave combustion method with the molar ratios of CU2＋ to Ni2＋ as 3：7, 4：6, 5：5, 6：4 and 7：3. The as-prepared samples were characterized by XRD, HR-SEM, EDX and V...Cu-Ni alloy nanoparticles were prepared by a microwave combustion method with the molar ratios of CU2＋ to Ni2＋ as 3：7, 4：6, 5：5, 6：4 and 7：3. The as-prepared samples were characterized by XRD, HR-SEM, EDX and VSM. XRD and EDX analyses suggest the formation of pure alloy powders. The average crystallite sizes were found to be in the range of 21.56-33.25 nm. HR-SEM images show the clustered/agglomerated particle-like morphology structure. VSM results reveal that for low Ni content （CusNis, Cu6Ni4 and Cu7Ni3）, the system shows paramagnetic behaviors, whereas for high Ni content （Cu3Ni7 and Cu4Ni6）, it becomes ferromagnetic.展开更多
Un-doped and Co-doped ZnO nanoparticles （NPs） with different weight ratios （0.5, 1.0, 1.5, and 2.0 wt% of Co） were synthesized by a facile and rapid microwave-assisted combustion method using urea as a fuel. The p...Un-doped and Co-doped ZnO nanoparticles （NPs） with different weight ratios （0.5, 1.0, 1.5, and 2.0 wt% of Co） were synthesized by a facile and rapid microwave-assisted combustion method using urea as a fuel. The prepared NPs were characterized by X-ray diffraction （XRD）, high resolution scanning electron microscopy （HR-SEM）, energy dispersive X-ray analysis （EDX）, diffuse reflectance spectroscopy （DRS）, photoluminescence （PL） spectroscopy and vibrating sample magnetometry （VSM）. XRD patterns refined by the Rietveld method indicated that Co-doped ZnO had a single pure phase with wurtzite structure suggesting that Co^2＋ ions would occupy Zn^2＋ ionic sites within the ZnO crystal lattice. Interestingly, the morphology was found to convert substantially from grains to nanoparticles with close-packed periodic array of hexagonal-like shape and then into randomly distributed spherical NPs with the variation of Co-content. The optical band gap estimated using DRS was found to be red-shifted from 3.22 eV for the un-doped ZnO NPs then decrease up to 2.88 eV with increasing Co-content. PL spectra showed a strong green emission band thus confirming the formation of pure single ZnO phase. Magnetic studies showed that Co-doped ZnO NPs exhibited room temperature ferromagnetism （RTFM） and that the saturation magnetization attained a maximum value of 2.203 × 10^-3 emu/g for the highest Co-content. The antibacterial studies performed against a set of bacterial strains showed that the 2.0 wt% Co-doped ZnO NPs possessed a greater antibacterial effect.展开更多
文摘Cu-Ni alloy nanoparticles were prepared by a microwave combustion method with the molar ratios of CU2＋ to Ni2＋ as 3：7, 4：6, 5：5, 6：4 and 7：3. The as-prepared samples were characterized by XRD, HR-SEM, EDX and VSM. XRD and EDX analyses suggest the formation of pure alloy powders. The average crystallite sizes were found to be in the range of 21.56-33.25 nm. HR-SEM images show the clustered/agglomerated particle-like morphology structure. VSM results reveal that for low Ni content （CusNis, Cu6Ni4 and Cu7Ni3）, the system shows paramagnetic behaviors, whereas for high Ni content （Cu3Ni7 and Cu4Ni6）, it becomes ferromagnetic.
文摘Un-doped and Co-doped ZnO nanoparticles （NPs） with different weight ratios （0.5, 1.0, 1.5, and 2.0 wt% of Co） were synthesized by a facile and rapid microwave-assisted combustion method using urea as a fuel. The prepared NPs were characterized by X-ray diffraction （XRD）, high resolution scanning electron microscopy （HR-SEM）, energy dispersive X-ray analysis （EDX）, diffuse reflectance spectroscopy （DRS）, photoluminescence （PL） spectroscopy and vibrating sample magnetometry （VSM）. XRD patterns refined by the Rietveld method indicated that Co-doped ZnO had a single pure phase with wurtzite structure suggesting that Co^2＋ ions would occupy Zn^2＋ ionic sites within the ZnO crystal lattice. Interestingly, the morphology was found to convert substantially from grains to nanoparticles with close-packed periodic array of hexagonal-like shape and then into randomly distributed spherical NPs with the variation of Co-content. The optical band gap estimated using DRS was found to be red-shifted from 3.22 eV for the un-doped ZnO NPs then decrease up to 2.88 eV with increasing Co-content. PL spectra showed a strong green emission band thus confirming the formation of pure single ZnO phase. Magnetic studies showed that Co-doped ZnO NPs exhibited room temperature ferromagnetism （RTFM） and that the saturation magnetization attained a maximum value of 2.203 × 10^-3 emu/g for the highest Co-content. The antibacterial studies performed against a set of bacterial strains showed that the 2.0 wt% Co-doped ZnO NPs possessed a greater antibacterial effect.
