Strengthening of aluminium alloys 7xxx through the imposition of severe plastic deformation supplemented by ageing treatments is a challenge due to the limited workability of these alloys in cold deformation regimes.T...Strengthening of aluminium alloys 7xxx through the imposition of severe plastic deformation supplemented by ageing treatments is a challenge due to the limited workability of these alloys in cold deformation regimes.This study aims to comprehensively investigate the strengthening of aluminium alloy 7005 through the imposition of severe plastic deformation supplemented by two different ageing treatments:pre-deformation artificial ageing or postdeformation natural ageing.For this purpose,microstructure evolutions of the alloy processed through mentioned procedures were studied using X-ray diffraction and scanning electron microscopy while the alloy strengthening was evaluated using Vickers hardness measurement.Results show that a superlative strengthening is obtained through the imposition of severe plastic deformation supplemented by post-deformation natural ageing.For instance,the yield strength of the alloy increases to more than 400 MPa,about one-third greater than the counterpart amount after the usual T6 treatment.This superlative strength mainly occurs due to refinement of grains,an increase of dislocation density and an increase of volume fraction of the precipitates that appeared during natural ageing.Considering the applied models,it is inferred that the increase of volume fraction of precipitates that appeared during natural ageing has a determinative role in the strengthening of the alloy.展开更多
Although excellent recyclability is one of the advantages of Al alloys, a recycling process can reduce different properties of these alloys by adding coarse AlFeSi particles into the alloys' microstructures. One o...Although excellent recyclability is one of the advantages of Al alloys, a recycling process can reduce different properties of these alloys by adding coarse AlFeSi particles into the alloys' microstructures. One of the well-known methods for modifying the microstructure of metallic materials is the imposition of severe plastic deformation(SPD). Nevertheless, the microstructure evolutions of recycled Al alloys containing extraordinary fractions of AlFeSi particles during SPD processing have seldom been considered. The aim of the present work is to study the microstructure evolution of a recycled Al–Fe–Si–Cu alloy during SPD processing. For this purpose, tubular specimens of the mentioned alloy were subjected to different numbers of passes of a recently developed SPD process called tube channel pressing(TCP); their microstructures were then studied using different techniques. The results show that coarse AlFeSi particles are fragmented into finer particles after processing by TCP. However, decomposition and dissolution of AlFeSi particles through TCP processing are negligible. In addition, TCP processing results in an increase in hardness of the alloy, which is attributed to the refinement of grains, to an increase of the dislocation density, and to the fragmentation of AlFeSi particles.展开更多
基金the research board of Ferdowsi University of Mashhad(FUM)for the financial support and the provision of research facilities used in this work through grant No.3/41681.
文摘Strengthening of aluminium alloys 7xxx through the imposition of severe plastic deformation supplemented by ageing treatments is a challenge due to the limited workability of these alloys in cold deformation regimes.This study aims to comprehensively investigate the strengthening of aluminium alloy 7005 through the imposition of severe plastic deformation supplemented by two different ageing treatments:pre-deformation artificial ageing or postdeformation natural ageing.For this purpose,microstructure evolutions of the alloy processed through mentioned procedures were studied using X-ray diffraction and scanning electron microscopy while the alloy strengthening was evaluated using Vickers hardness measurement.Results show that a superlative strengthening is obtained through the imposition of severe plastic deformation supplemented by post-deformation natural ageing.For instance,the yield strength of the alloy increases to more than 400 MPa,about one-third greater than the counterpart amount after the usual T6 treatment.This superlative strength mainly occurs due to refinement of grains,an increase of dislocation density and an increase of volume fraction of the precipitates that appeared during natural ageing.Considering the applied models,it is inferred that the increase of volume fraction of precipitates that appeared during natural ageing has a determinative role in the strengthening of the alloy.
基金the research board of Ferdowsi University of Mashhad(FUM)for the financial supportthe provision of research facilities used in this work through grant number 2/43989
文摘Although excellent recyclability is one of the advantages of Al alloys, a recycling process can reduce different properties of these alloys by adding coarse AlFeSi particles into the alloys' microstructures. One of the well-known methods for modifying the microstructure of metallic materials is the imposition of severe plastic deformation(SPD). Nevertheless, the microstructure evolutions of recycled Al alloys containing extraordinary fractions of AlFeSi particles during SPD processing have seldom been considered. The aim of the present work is to study the microstructure evolution of a recycled Al–Fe–Si–Cu alloy during SPD processing. For this purpose, tubular specimens of the mentioned alloy were subjected to different numbers of passes of a recently developed SPD process called tube channel pressing(TCP); their microstructures were then studied using different techniques. The results show that coarse AlFeSi particles are fragmented into finer particles after processing by TCP. However, decomposition and dissolution of AlFeSi particles through TCP processing are negligible. In addition, TCP processing results in an increase in hardness of the alloy, which is attributed to the refinement of grains, to an increase of the dislocation density, and to the fragmentation of AlFeSi particles.