Designing and synthesis of cost effective bulk metallic glasses （BMGs） has been of considerable interest during the last decade so that they can be made commercially viable. Among these, Zr-based BMGs have been repo...Designing and synthesis of cost effective bulk metallic glasses （BMGs） has been of considerable interest during the last decade so that they can be made commercially viable. Among these, Zr-based BMGs have been reported extensively due to their attractive properties, An alloy having composition Zr65Cu18Ni9A18 was designed and synthesized using 2-3 N pure materials by Cu mould casting. The alloy was characterized by X- ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive X-ray spectroscopy （EDS） and high temperature differential scanning calorimetry （DSC）. Thermal parameters like supercooled liquid region △Tx, reduced glass transition temperature Trg, γ and δ parameters were evaluated. Mechanical properties like microhardness, nanohardness, elastic modulus and fracture strength were measured. The alloy showed wide supercooled liquid region of 129＋1 K with improved thermal stability. The alloy has considerable fracture strength along with fair amount of ductility.展开更多
Results regarding best approximation and best Simultaneous approximation on convex metric spaces are Obtained.Existence of fixed points for an ultimately nonexpansive semigroup of mappings is also shown.
基金The National Natural Science Foundation of China （50471077） the Ministry of Science and Technology of China （2006CB605201, 2005DFA50860） supported this work.
文摘Designing and synthesis of cost effective bulk metallic glasses （BMGs） has been of considerable interest during the last decade so that they can be made commercially viable. Among these, Zr-based BMGs have been reported extensively due to their attractive properties, An alloy having composition Zr65Cu18Ni9A18 was designed and synthesized using 2-3 N pure materials by Cu mould casting. The alloy was characterized by X- ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive X-ray spectroscopy （EDS） and high temperature differential scanning calorimetry （DSC）. Thermal parameters like supercooled liquid region △Tx, reduced glass transition temperature Trg, γ and δ parameters were evaluated. Mechanical properties like microhardness, nanohardness, elastic modulus and fracture strength were measured. The alloy showed wide supercooled liquid region of 129＋1 K with improved thermal stability. The alloy has considerable fracture strength along with fair amount of ductility.
文摘Results regarding best approximation and best Simultaneous approximation on convex metric spaces are Obtained.Existence of fixed points for an ultimately nonexpansive semigroup of mappings is also shown.