Nanocrystalline zirconia powder with high surface area and high tetragonal phase percentage is prepared by the precipitation method using ammonium hydroxide as a precipitating agent. The pH of precipitation, preparati...Nanocrystalline zirconia powder with high surface area and high tetragonal phase percentage is prepared by the precipitation method using ammonium hydroxide as a precipitating agent. The pH of precipitation, preparation temperature and calcinations＇ temperature are optimized.Crystallite size, specific surface area, tetragonal phase percentage and the thermal stability of the prepared samples are identified by diferent characterization tools such as X-ray difraction（XRD）, thermo gravimetric analysis（TGA）, diferential scanning calorimetry（DSC）, BET surface area, scanning electron microscopy（SEM） and transmission electron microscopy（TEM）. The optimum preparation parameters for obtaining nanocrystalline zirconia with high percentage of tetragonal phase and high surface area are pH 9, preparation temperature of 80℃ and calcinations＇ temperature of 400℃. The sample prepared under optimized conditions showed a high specific surface area of 179.2 m2/g, high tetragonal phase percentage of 81% and high catalytic activity（60%） for synthesis of butyl acetate ester.展开更多
Highly active mesoporous TiO_2 of about 6 nm crystal size and 280.7 m^2/g specific surface areas has been successfully synthesized via controlled hydrolysis of titanium butoxide at acidic medium. It was characterized ...Highly active mesoporous TiO_2 of about 6 nm crystal size and 280.7 m^2/g specific surface areas has been successfully synthesized via controlled hydrolysis of titanium butoxide at acidic medium. It was characterized by means of XRD（X-ray diffraction）, SEM（scanning electron microscopy）, TEM（transmission electron microscopy）, FT-IR（Fourier transform infrared spectroscopy）, TGA（thermogravimetric analysis）, DSC（differential scanning calorimetry） and BET（Brunauer–Emmett–Teller） surface area. The degradation of dichlorophenol-indophenol（DCPIP） under ultraviolet（UV） light was studied to evaluate the photocatalytic activity of samples. The effects of different parameters and kinetics were investigated. Accordingly, a complete degradation of DCPIP dye was achieved by applying the optimal operational conditions of 1 g/L of catalyst, 10 mg/L of DCPIP, pH of 3 and the temperature at 25 ± 3°C after 3 min under UV irradiation. Meanwhile, the Langmuir–Hinshelwood kinetic model described the variations in pure photocatalytic branch in consistent with a first order power law model.The results proved that the prepared TiO_2 nanoparticle has a photocatalytic activity significantly better than Degussa P-25.展开更多
文摘Nanocrystalline zirconia powder with high surface area and high tetragonal phase percentage is prepared by the precipitation method using ammonium hydroxide as a precipitating agent. The pH of precipitation, preparation temperature and calcinations＇ temperature are optimized.Crystallite size, specific surface area, tetragonal phase percentage and the thermal stability of the prepared samples are identified by diferent characterization tools such as X-ray difraction（XRD）, thermo gravimetric analysis（TGA）, diferential scanning calorimetry（DSC）, BET surface area, scanning electron microscopy（SEM） and transmission electron microscopy（TEM）. The optimum preparation parameters for obtaining nanocrystalline zirconia with high percentage of tetragonal phase and high surface area are pH 9, preparation temperature of 80℃ and calcinations＇ temperature of 400℃. The sample prepared under optimized conditions showed a high specific surface area of 179.2 m2/g, high tetragonal phase percentage of 81% and high catalytic activity（60%） for synthesis of butyl acetate ester.
基金funded by the Science and Technology Development Fund (STDF), Ministry of Scientific Research (No. 1414, "Quantum Dots Nanomaterials Dye Sensitized Solar Cells")
文摘Highly active mesoporous TiO_2 of about 6 nm crystal size and 280.7 m^2/g specific surface areas has been successfully synthesized via controlled hydrolysis of titanium butoxide at acidic medium. It was characterized by means of XRD（X-ray diffraction）, SEM（scanning electron microscopy）, TEM（transmission electron microscopy）, FT-IR（Fourier transform infrared spectroscopy）, TGA（thermogravimetric analysis）, DSC（differential scanning calorimetry） and BET（Brunauer–Emmett–Teller） surface area. The degradation of dichlorophenol-indophenol（DCPIP） under ultraviolet（UV） light was studied to evaluate the photocatalytic activity of samples. The effects of different parameters and kinetics were investigated. Accordingly, a complete degradation of DCPIP dye was achieved by applying the optimal operational conditions of 1 g/L of catalyst, 10 mg/L of DCPIP, pH of 3 and the temperature at 25 ± 3°C after 3 min under UV irradiation. Meanwhile, the Langmuir–Hinshelwood kinetic model described the variations in pure photocatalytic branch in consistent with a first order power law model.The results proved that the prepared TiO_2 nanoparticle has a photocatalytic activity significantly better than Degussa P-25.