The effect of extrusion on grain refinement has been studied in the AZ91 cast ingots. It is found that grain sizesmaller than 10μm can be obtained by the extrusion processing. Vickers hardness measurements were also ...The effect of extrusion on grain refinement has been studied in the AZ91 cast ingots. It is found that grain sizesmaller than 10μm can be obtained by the extrusion processing. Vickers hardness measurements were also carriedout to evaluate the effect of these processes on the room temperature mechanical properties. The experimentalresults of high temperature tensile tests revealed that the stress was inversely proportional to the square of the grainsize and that the activation energy for superplastic flow was higher than that for grain boundary diffusion.展开更多
The solution-treated Mg-4Y-4Sm-0.5Zr alloy was extruded at temperatures from 325℃ to 500℃.Dynamic recrystallization(DRX) completely occurs when the alloy is extruded at 350℃and above.The grains of the extruded allo...The solution-treated Mg-4Y-4Sm-0.5Zr alloy was extruded at temperatures from 325℃ to 500℃.Dynamic recrystallization(DRX) completely occurs when the alloy is extruded at 350℃and above.The grains of the extruded alloy are obviously refined by the occurrence of DRX.The average grain size of the extruded alloy increases with increasing the extrusion temperature,leading to a slight decrease of the ultimate tensile strength(UTS) and the yield strength(YS) .On the contrary,the UTS and YS of the extruded and aged alloy increase with increasing the extrusion temperature.Values of UTS of 400 MPa,YS larger than 300 MPa and elongation(EL) of 7%are achieved after extrusion at 400℃ and ageing at 200℃ for 16 h.Both grain refinement and precipitation are efficient strengthening mechanisms for the Mg-4Y-4Sm-0.5Zr alloy.展开更多
基金The autlors gratefully acknowledge the financial support from the National Commnittee for High Technology ResearchDevelopment of China under the project No.2002AA331120.
文摘The effect of extrusion on grain refinement has been studied in the AZ91 cast ingots. It is found that grain sizesmaller than 10μm can be obtained by the extrusion processing. Vickers hardness measurements were also carriedout to evaluate the effect of these processes on the room temperature mechanical properties. The experimentalresults of high temperature tensile tests revealed that the stress was inversely proportional to the square of the grainsize and that the activation energy for superplastic flow was higher than that for grain boundary diffusion.
基金Project(2009AA033501)supported by the National Hi-tech Research and Development Program of ChinaProject(2006BAE04B01-2)supported by the National Key Technology Research&Development Program of ChinaProject(06SR07104)supported by theInternational Cooperation Fund of Shanghai Science and Technology Committee,Shanghai/Rhone-Alpes Science and Technology
文摘The solution-treated Mg-4Y-4Sm-0.5Zr alloy was extruded at temperatures from 325℃ to 500℃.Dynamic recrystallization(DRX) completely occurs when the alloy is extruded at 350℃and above.The grains of the extruded alloy are obviously refined by the occurrence of DRX.The average grain size of the extruded alloy increases with increasing the extrusion temperature,leading to a slight decrease of the ultimate tensile strength(UTS) and the yield strength(YS) .On the contrary,the UTS and YS of the extruded and aged alloy increase with increasing the extrusion temperature.Values of UTS of 400 MPa,YS larger than 300 MPa and elongation(EL) of 7%are achieved after extrusion at 400℃ and ageing at 200℃ for 16 h.Both grain refinement and precipitation are efficient strengthening mechanisms for the Mg-4Y-4Sm-0.5Zr alloy.