During the last two decades,many algorithms were developed to simulate the solidification process for different casting methods like ingots,continuous casting of steel and the direct chill cast of aluminum.Experiments...During the last two decades,many algorithms were developed to simulate the solidification process for different casting methods like ingots,continuous casting of steel and the direct chill cast of aluminum.Experiments performed under exactly known conditions and with the detailed knowledge of meso-and micro-structures are required for validating these simulations.The aim of this paper is to give a data set to validate these simulations.Unidirectional solidification experiments were performed by using a rotating magnetic field(RMF)to study the effect of melt flow on the solidified micro-and meso-structure of the Al-7wt.%Si binary alloy.The first and the third 1/3 parts of samples were solidified without magnetic stirring,and the second(middle)1/3 part was solidified by using magnetic stirring.The magnetic induction was 10 m T,the temperature gradient was~7 K/mm,and the sample movement velocity was 0.1 mm/s.On the longitudinal section of the sample,the columnar/equiaxed transition(CET),the equiaxed/columnar transition(ECT),the secondary dendrite arm spacing(SDAS),and the macrosegregation(concentration distribution and the amount of eutectic)were investigated.The primary dendrite arm spacing(PDAS)and the grain structure were studied on the cross-section after color etching.展开更多
基金financially supported by the project entitled“Formation of as-solidified structure and macrosegregation during unidirectional solidification under controlled flow conditions”of the National Research Development,and Investigation Office(No.130946)。
文摘During the last two decades,many algorithms were developed to simulate the solidification process for different casting methods like ingots,continuous casting of steel and the direct chill cast of aluminum.Experiments performed under exactly known conditions and with the detailed knowledge of meso-and micro-structures are required for validating these simulations.The aim of this paper is to give a data set to validate these simulations.Unidirectional solidification experiments were performed by using a rotating magnetic field(RMF)to study the effect of melt flow on the solidified micro-and meso-structure of the Al-7wt.%Si binary alloy.The first and the third 1/3 parts of samples were solidified without magnetic stirring,and the second(middle)1/3 part was solidified by using magnetic stirring.The magnetic induction was 10 m T,the temperature gradient was~7 K/mm,and the sample movement velocity was 0.1 mm/s.On the longitudinal section of the sample,the columnar/equiaxed transition(CET),the equiaxed/columnar transition(ECT),the secondary dendrite arm spacing(SDAS),and the macrosegregation(concentration distribution and the amount of eutectic)were investigated.The primary dendrite arm spacing(PDAS)and the grain structure were studied on the cross-section after color etching.