To improve the oxidation resistance and corrosion resistance of Zr-4 alloy, titanium nitride （TIN） coatings were prepared on the Zr-4 alloy with a TiN ceramic target with different ratios of N2. Microstructure and h...To improve the oxidation resistance and corrosion resistance of Zr-4 alloy, titanium nitride （TIN） coatings were prepared on the Zr-4 alloy with a TiN ceramic target with different ratios of N2. Microstructure and high-temperature properties of the TiN coated samples were studied by scanning electron microscopy （SEM）, energy dispersive spectrometer （EDS）, X-ray diffraction meter （XRD）, X-ray photoelectron spectroscopy （XPS）, heat treatment furnace and autoclaves, respectively. The x value of the TiN coatings （TiN） ranges from 0.96 to 1.33. After the introduction of N2, TiN coating exhibits a weak （200） plane and a preferred （111） orientation. The coating prepared with an N2 flow ratio of 15% shows an optimal oxidation resistance in the atmospheric environment at 800 ℃. In either 1 200 ℃ steam environment for one hour, or deionized water at 360 ℃ and a pressure of 18.6 Mpa for 16 d, the opitimized TiN coated samples have no delamination or spallation; and the gains in the masses of samples are much smaller than Zr-4 alloy. These results demonstrate the effectiveness of the optimized TiN coating as the protective coating on the Zr-4 alloy under extreme conditons.展开更多
基金Funded by the National Science and Technology Major Project of the Ministry of Science and Technology of China(2015ZX06004001-002)the Postgraduate Research and Innovation Project of the University of South China(2017XCX11)
文摘To improve the oxidation resistance and corrosion resistance of Zr-4 alloy, titanium nitride （TIN） coatings were prepared on the Zr-4 alloy with a TiN ceramic target with different ratios of N2. Microstructure and high-temperature properties of the TiN coated samples were studied by scanning electron microscopy （SEM）, energy dispersive spectrometer （EDS）, X-ray diffraction meter （XRD）, X-ray photoelectron spectroscopy （XPS）, heat treatment furnace and autoclaves, respectively. The x value of the TiN coatings （TiN） ranges from 0.96 to 1.33. After the introduction of N2, TiN coating exhibits a weak （200） plane and a preferred （111） orientation. The coating prepared with an N2 flow ratio of 15% shows an optimal oxidation resistance in the atmospheric environment at 800 ℃. In either 1 200 ℃ steam environment for one hour, or deionized water at 360 ℃ and a pressure of 18.6 Mpa for 16 d, the opitimized TiN coated samples have no delamination or spallation; and the gains in the masses of samples are much smaller than Zr-4 alloy. These results demonstrate the effectiveness of the optimized TiN coating as the protective coating on the Zr-4 alloy under extreme conditons.