The structure of SEN and upper nozzles was optimized and simulated. Relevant trials were conducted on site during thecasting of Al-killed steel. These optimizations effectively solve the nozzle clogging and reduce the...The structure of SEN and upper nozzles was optimized and simulated. Relevant trials were conducted on site during thecasting of Al-killed steel. These optimizations effectively solve the nozzle clogging and reduce the defects of the casting slab.展开更多
Based on the refractories research of Baosteel, the demands for refractories from the developing steel-making technology as high security, high efficiency, energy saving and environment .friendly are introduced.
Monolithic stoppers play a very important role in continuous casting（ short for CC）. Sometimes,the stopper slag line is seriously eroded and broken,CC has to pause. The research shows that there are three main reaso...Monolithic stoppers play a very important role in continuous casting（ short for CC）. Sometimes,the stopper slag line is seriously eroded and broken,CC has to pause. The research shows that there are three main reasons which bring severe erosion of monolithic stopper slag line. Firstly,much Fe_2O_3 and MnO in slag react with carbon（ C） in the stopper,C is gradually eroded and erosion resistance of the stopper greatly weakens. Secondly,F increase in tundish covering flux will quicken erosion of the stopper slag line. Thirdly, High LOI of tundish covering flux also makes erosion of the stopper slag line speed up. On one hand,CaCO_3 in tundish covering flux decomposes and brings CO_2; on the other hand,minerals with water in tundish covering flux decompose at high temperatures and bring water vapor.Then CO_2 and water vapor react with C in the stopper,C is gradually eroded,aggravating the erosion.展开更多
文摘The structure of SEN and upper nozzles was optimized and simulated. Relevant trials were conducted on site during thecasting of Al-killed steel. These optimizations effectively solve the nozzle clogging and reduce the defects of the casting slab.
文摘Based on the refractories research of Baosteel, the demands for refractories from the developing steel-making technology as high security, high efficiency, energy saving and environment .friendly are introduced.
文摘Monolithic stoppers play a very important role in continuous casting（ short for CC）. Sometimes,the stopper slag line is seriously eroded and broken,CC has to pause. The research shows that there are three main reasons which bring severe erosion of monolithic stopper slag line. Firstly,much Fe_2O_3 and MnO in slag react with carbon（ C） in the stopper,C is gradually eroded and erosion resistance of the stopper greatly weakens. Secondly,F increase in tundish covering flux will quicken erosion of the stopper slag line. Thirdly, High LOI of tundish covering flux also makes erosion of the stopper slag line speed up. On one hand,CaCO_3 in tundish covering flux decomposes and brings CO_2; on the other hand,minerals with water in tundish covering flux decompose at high temperatures and bring water vapor.Then CO_2 and water vapor react with C in the stopper,C is gradually eroded,aggravating the erosion.