Dynamic recrystallization behavior and mechanical properties of bimodal scale Al2O3 reinforced AZ31 composites by soild state synthesis

In this paper,(500 nm 1%+5μm 3%)bimodal scale Al2O3p/AZ31 composites was fabricated by solid state synthesis and the effect of bimodal scale Al2O3 particulates on its dynamic recrystallization behavior and mechanical properties was investigated.The optical microscopy,scanning electron microscopy,transmission electron microscopy and electron universal strength tester composites were used to characterize the composites.The results indicate that the grains size of the composites are significantly refined and the mechanical properties are obviously improved.Due to the presence of the bimodal scale Al2o3 particulates,the high-density dislocation zone is formed around nano-Al2o3p and the particle deformation zone is formed near micron-ABOap.These zones are ideal sites for the formation of recrystallization nucleus.Meanwhile,the addition of the bimodal scale Al2o3 particulates may delay or hinder the growth of matrix grain through the pining effect on the grain boundaries,resulting in significantly improving the yield strength and tensile strength of Al2O3p/AZ31 composites.

Effect of glucose concentrations on wear resistance of Al/APC composites prepared by hydrothermal carbonized deposition on chips

In this study,a novel method termed hydrothermal carbonized deposition on chips(HTCDC)is proposed to prepare aluminum alloy-amorphous carbon(Al/APC)composites.The influences of glucose concentration in hydrothermally reaction on the microstructure and wear resistance of the Al/APC composites were thoroughly studied.Amorphous carbon was deposited by HTCDC onto Al–20Si chips as a supporter.The Al/APC composites were prepared by hot extrusion from the chips.The results indicated that a uniform carbon film was successfully synthesized on the surface of the chips,improving the wear resistance of the Al/APC composites.With increasing concentration of glucose solution,the size and the number of delamination on the wear surface and the coefficient of friction decreased,and the wear rate decreased at first and then increased.In addition,the dehydration and carbonization processes in the hydrothermal reaction of glucose were analyzed.A schematic model of the wear surface of the Al/APC composites was established and the wear mechanisms were discussed.