Nitrogen removal from ammonium-containing wastewater was conducted using polylactic acid （PLA）/ starch blends as carbon source and carrier for fimctional bacteria. The exclusive and interactive influences of operati...Nitrogen removal from ammonium-containing wastewater was conducted using polylactic acid （PLA）/ starch blends as carbon source and carrier for fimctional bacteria. The exclusive and interactive influences of operating parameters （i.e., temperature, pH, stirring rate, and PLA-to-starch ratio （PLA proportion）） on nitrification （Y1）, denitrification （Y2）, and COD release rates （Y3） were investigated through response surface methodology. Experimental results indicated that nitrogen removal could be successfully achieved in the PLA/starch blends through simultaneous mtnncatlon anti clenltnncatlon. The carbon release rate of the blends was controllable. The sensitivity of Y1, Y2, and Y3 to different operating parameters also differed. The sequence for each response was as follows： for Y1, pH 〉 stirring rate 〉 PLA proportion 〉 temperature; for Y2, PH 〉 PLA proportion 〉.temperature.〉 stirring rate; and for Y3, stirring rate 〉pH 〉 PLA proportion 〉 temperature. In this study, the following optimum conditions were observed： temperature, 32.0℃; pH 7.7; stirring rate, 200.0 r · min^-1 and PLA proportion 0.4. Under these conditions Y1 Y2 and Y3 were 134.0 μg-N·g-blend^-1·h^-1, 160.9μg-N-g-blend^-1·h^-1, and 7.6 × 10^3 μg-O·g-blend^-1·h^-1, respectively. These results suggested that the PLA/starch blends may be an ideal packing material for nitrogen removal.展开更多
基金This study was supported by the National Natural Science Foundation of China （Grant No. 41505124） and Fundamental Research Funds for the Central Universities （Grant No. FRF-TP- 15 -044A 1）.
文摘Nitrogen removal from ammonium-containing wastewater was conducted using polylactic acid （PLA）/ starch blends as carbon source and carrier for fimctional bacteria. The exclusive and interactive influences of operating parameters （i.e., temperature, pH, stirring rate, and PLA-to-starch ratio （PLA proportion）） on nitrification （Y1）, denitrification （Y2）, and COD release rates （Y3） were investigated through response surface methodology. Experimental results indicated that nitrogen removal could be successfully achieved in the PLA/starch blends through simultaneous mtnncatlon anti clenltnncatlon. The carbon release rate of the blends was controllable. The sensitivity of Y1, Y2, and Y3 to different operating parameters also differed. The sequence for each response was as follows： for Y1, pH 〉 stirring rate 〉 PLA proportion 〉 temperature; for Y2, PH 〉 PLA proportion 〉.temperature.〉 stirring rate; and for Y3, stirring rate 〉pH 〉 PLA proportion 〉 temperature. In this study, the following optimum conditions were observed： temperature, 32.0℃; pH 7.7; stirring rate, 200.0 r · min^-1 and PLA proportion 0.4. Under these conditions Y1 Y2 and Y3 were 134.0 μg-N·g-blend^-1·h^-1, 160.9μg-N-g-blend^-1·h^-1, and 7.6 × 10^3 μg-O·g-blend^-1·h^-1, respectively. These results suggested that the PLA/starch blends may be an ideal packing material for nitrogen removal.