A new photocatalytic activity (PC) measurement instrument based on the measurement of the photo-induced reduction of Ag ions was proposed. The feature of this system is to perform “ultraviolet irradiation for PC acti...A new photocatalytic activity (PC) measurement instrument based on the measurement of the photo-induced reduction of Ag ions was proposed. The feature of this system is to perform “ultraviolet irradiation for PC activation” and “Ag film thickness determination for PC evaluation” simultaneously and automatically. Realizing a PC measurement system with high sensitivity, wide dynamic range, easy operation and reproducibility, which is especially suited for the PC measurement of the coatings on transparent substrates.展开更多
Photo catalytic TiO2 coatings with well defined honeycomb structure were successfully self-assembled on glass substrates by a simple “dip and burn solgel method“. The crux of this new method is that the starting mat...Photo catalytic TiO2 coatings with well defined honeycomb structure were successfully self-assembled on glass substrates by a simple “dip and burn solgel method“. The crux of this new method is that the starting material for the sol-gel coating (the water solution of ammonium titanium citrate) was “doped” with “tea-leaf extracts”. Tea-leaf extracts were completely dissolved in the water solution of ammonium titanium citrate and nucleate uniformly during the drying procedure of the coating precursor formation. This uniformly dispersed nucleation of the “tea-leaf extracts (tannin, catechin…)” were extracted during calcinations and leaving honeycomb-cell like nano-structure in the TiO2 coatings. Self-assembled cells were uniformly distributed in the TiO2 coatings and the diameter of the cells was in the range of 200 - 1000 nm. Fine honeycomb structures were clearly observed with microscopic observations.展开更多
文摘A new photocatalytic activity (PC) measurement instrument based on the measurement of the photo-induced reduction of Ag ions was proposed. The feature of this system is to perform “ultraviolet irradiation for PC activation” and “Ag film thickness determination for PC evaluation” simultaneously and automatically. Realizing a PC measurement system with high sensitivity, wide dynamic range, easy operation and reproducibility, which is especially suited for the PC measurement of the coatings on transparent substrates.
文摘Photo catalytic TiO2 coatings with well defined honeycomb structure were successfully self-assembled on glass substrates by a simple “dip and burn solgel method“. The crux of this new method is that the starting material for the sol-gel coating (the water solution of ammonium titanium citrate) was “doped” with “tea-leaf extracts”. Tea-leaf extracts were completely dissolved in the water solution of ammonium titanium citrate and nucleate uniformly during the drying procedure of the coating precursor formation. This uniformly dispersed nucleation of the “tea-leaf extracts (tannin, catechin…)” were extracted during calcinations and leaving honeycomb-cell like nano-structure in the TiO2 coatings. Self-assembled cells were uniformly distributed in the TiO2 coatings and the diameter of the cells was in the range of 200 - 1000 nm. Fine honeycomb structures were clearly observed with microscopic observations.