A mesoporous UiO-66-NH_(2) aerogel is prepared via a straightforward sol-gel method without using any binders or mechanical pressures, in which the amine groups are directly introduced into the matrix by using 2-amino...A mesoporous UiO-66-NH_(2) aerogel is prepared via a straightforward sol-gel method without using any binders or mechanical pressures, in which the amine groups are directly introduced into the matrix by using 2-aminoterephthalic acid. The novel UiO-66-NH_(2) aerogel also exhibits high specific surface area and mesopore-dominated structure, implying its highly potential use in CO_(2) adsorption. For ulteriorly investigating the effect of amine loading on the CO_(2) adsorption ability, a series of UiO-66-NH_(2) aerogel with different amino content is fabricated by changing the ligand/metal molar ratio. When the molar ratio is 1.45, the CO_(2) adsorption capacity reaches the optimum value of 2.13 mmol·g^(-1) at 25 ℃ and 0.1 MPa, which is 12.2% higher than that of pure UiO-66 aerogel. Additionally, UiO-66-NH_(2)-1.45 aerogel also has noticeable CO_(2) selectivity against N_(2) and CH_(4) as well as good regeneration stability. Such results imply that it has good application prospect in the field of CO_(2) adsorption, and also contains the potential to be applied in catalysis, separation and other fields.展开更多
基金supported by the National Natural Science Foundation of China (21603125)Science-Education-Industry Integration Innovation Pilot Project of Qilu University of Technology (2020KJC-GH13)+2 种基金International Cooperation Project of Shandong Academy of Sciences (2019GHPY09)Natural Science Foundation of Shandong Province (ZR2019BEM025)Young doctor Cooperation Foundation of Qilu University of Technology (Shandong Academy of Sciences) (2019BSHZ0016)。
文摘A mesoporous UiO-66-NH_(2) aerogel is prepared via a straightforward sol-gel method without using any binders or mechanical pressures, in which the amine groups are directly introduced into the matrix by using 2-aminoterephthalic acid. The novel UiO-66-NH_(2) aerogel also exhibits high specific surface area and mesopore-dominated structure, implying its highly potential use in CO_(2) adsorption. For ulteriorly investigating the effect of amine loading on the CO_(2) adsorption ability, a series of UiO-66-NH_(2) aerogel with different amino content is fabricated by changing the ligand/metal molar ratio. When the molar ratio is 1.45, the CO_(2) adsorption capacity reaches the optimum value of 2.13 mmol·g^(-1) at 25 ℃ and 0.1 MPa, which is 12.2% higher than that of pure UiO-66 aerogel. Additionally, UiO-66-NH_(2)-1.45 aerogel also has noticeable CO_(2) selectivity against N_(2) and CH_(4) as well as good regeneration stability. Such results imply that it has good application prospect in the field of CO_(2) adsorption, and also contains the potential to be applied in catalysis, separation and other fields.