An organo-montmorillonite-supported nanoscale zero-valent iron material （M-NZVI） was synthesized to degrade decabromodiphenyl ether （BDE-209）. The results showed that nanoscale zero-valent iron had good dispersion...An organo-montmorillonite-supported nanoscale zero-valent iron material （M-NZVI） was synthesized to degrade decabromodiphenyl ether （BDE-209）. The results showed that nanoscale zero-valent iron had good dispersion on organo-montmoriUonite and was present as a core-shell structure with a particle size range of nanoscale iron between 30-90 nm, characterized by XRD, SEM, TEM, XRF, ICP-AES, and XPS. The results of the degradation of BDE-209 by M-NZVI showed that the efficiency of M-NZVI in removing BDE-209 was much higher than that of NZVI. The efficiency of M-NZVI in removing BDE-209 decreased as the pH and the initial dissolved oxygen content of the reaction solution increased, but increased as the proportion of water in the reaction solution increased.展开更多
基金supported by the National Science and Technology Major Projects of Water Pollution Control andManagement of China (No. 2012ZX07206002)
文摘An organo-montmorillonite-supported nanoscale zero-valent iron material （M-NZVI） was synthesized to degrade decabromodiphenyl ether （BDE-209）. The results showed that nanoscale zero-valent iron had good dispersion on organo-montmoriUonite and was present as a core-shell structure with a particle size range of nanoscale iron between 30-90 nm, characterized by XRD, SEM, TEM, XRF, ICP-AES, and XPS. The results of the degradation of BDE-209 by M-NZVI showed that the efficiency of M-NZVI in removing BDE-209 was much higher than that of NZVI. The efficiency of M-NZVI in removing BDE-209 decreased as the pH and the initial dissolved oxygen content of the reaction solution increased, but increased as the proportion of water in the reaction solution increased.