To reduce the sensitivity of grain growth to sintering temperature for improving property consistency of sintered Nd-Fe-B magnets, combined additions of Zr and Nb were investigated. It was found that when Zr content w...To reduce the sensitivity of grain growth to sintering temperature for improving property consistency of sintered Nd-Fe-B magnets, combined additions of Zr and Nb were investigated. It was found that when Zr content was increased to 0.07 at. pct, abnormal grain growth was effectively hindered even when the sintering temperature reached 1100℃. With combined additions of 0.07 at. pct Zr and 0.07 at. pct Nb, the sensitivity of grain growth to sintering temperature was greatly reduced consistency than the magnets containing no Zr and also improved. The magnets sintered at 1100℃ showed higher property Nb. In addition, the magnetic properties of magnets were also improved.展开更多
基金supported by the National Natural Science Foundation of China(No.50701039)Program forNew Century Excellent Talents in University(No.05–0526)Program for Innovative Research Team in University(No.0651)
文摘To reduce the sensitivity of grain growth to sintering temperature for improving property consistency of sintered Nd-Fe-B magnets, combined additions of Zr and Nb were investigated. It was found that when Zr content was increased to 0.07 at. pct, abnormal grain growth was effectively hindered even when the sintering temperature reached 1100℃. With combined additions of 0.07 at. pct Zr and 0.07 at. pct Nb, the sensitivity of grain growth to sintering temperature was greatly reduced consistency than the magnets containing no Zr and also improved. The magnets sintered at 1100℃ showed higher property Nb. In addition, the magnetic properties of magnets were also improved.