Heat treatment of metal-organic frameworks(MOFs)has provided a wide variety of functional carbons coordinated with metal compounds.In this study,two kinds of zinc-based MOF(ZMOF),C_(16)H_(10)O_(4)Zn(ZMOF1)and C_(8)H_(...Heat treatment of metal-organic frameworks(MOFs)has provided a wide variety of functional carbons coordinated with metal compounds.In this study,two kinds of zinc-based MOF(ZMOF),C_(16)H_(10)O_(4)Zn(ZMOF1)and C_(8)H_(4)O_(4)Zn(ZMOF2),were prepared.ZMOF1 and ZMOF2 were carbonized at 1000℃,forming CZMOF1 and CZMOF2,respectively.The specific surface area(S_(BET))of CZMOF2 was~2700 m^(2)g^(−1),much higher than that of CZMOF1(~1300 m^(2)g^(−1)).A supercapacitor electrode based on CZMOF2 achieved specific capacitances of 360,278,and 221 F g^(−1)at 50,250,and 1000 mA g^(−1)in an aqueous electrolyte(H2SO_(4)),respectively,the highest values reported to date for ZMOF-derived electrodes under identical conditions.The practical applicability of the CZMOF-based supercapacitor was verified in non-aqueous electrolytes.The initial capacitance retention was 78%after 100000 charge/discharge cycles at 10 A g^(−1).Crucially,the high capacitance of CZMOF2 arises from pore generation during carbonization.Below 1000℃,pore generation is dominated by the Zn/C ratio of ZMOFs,as carbon atoms reduce the zinc oxides formed during carbonization.Above 1000℃,a high O/C ratio becomes essential for pore generation because the oxygen functional groups are pyrolyzed.These findings will provide insightful information for other metal-based MOFderived multifunctional carbons.展开更多
基金partially supported by a Grant-in-Aid for Scientific Research(KAKENHI)from the Japan Society for the Promotion of Science(JSPS)(grant number 19H05332)。
文摘Heat treatment of metal-organic frameworks(MOFs)has provided a wide variety of functional carbons coordinated with metal compounds.In this study,two kinds of zinc-based MOF(ZMOF),C_(16)H_(10)O_(4)Zn(ZMOF1)and C_(8)H_(4)O_(4)Zn(ZMOF2),were prepared.ZMOF1 and ZMOF2 were carbonized at 1000℃,forming CZMOF1 and CZMOF2,respectively.The specific surface area(S_(BET))of CZMOF2 was~2700 m^(2)g^(−1),much higher than that of CZMOF1(~1300 m^(2)g^(−1)).A supercapacitor electrode based on CZMOF2 achieved specific capacitances of 360,278,and 221 F g^(−1)at 50,250,and 1000 mA g^(−1)in an aqueous electrolyte(H2SO_(4)),respectively,the highest values reported to date for ZMOF-derived electrodes under identical conditions.The practical applicability of the CZMOF-based supercapacitor was verified in non-aqueous electrolytes.The initial capacitance retention was 78%after 100000 charge/discharge cycles at 10 A g^(−1).Crucially,the high capacitance of CZMOF2 arises from pore generation during carbonization.Below 1000℃,pore generation is dominated by the Zn/C ratio of ZMOFs,as carbon atoms reduce the zinc oxides formed during carbonization.Above 1000℃,a high O/C ratio becomes essential for pore generation because the oxygen functional groups are pyrolyzed.These findings will provide insightful information for other metal-based MOFderived multifunctional carbons.