We reported a facile preparation of a uniform decoration of spherical n-type SnO2 by p-type CuO nanopa rticles as well as their utilization for enhanced performance on toluene gas detection.CuO nanoparticles and spher...We reported a facile preparation of a uniform decoration of spherical n-type SnO2 by p-type CuO nanopa rticles as well as their utilization for enhanced performance on toluene gas detection.CuO nanoparticles and spherical SnO2 were synthesized by a facile non-hydrolytic solvothermal reaction,which could easily control their morphology.A uniform CuO nanoparticles decoration onto spherical SnO2 was achieved by a simple sonication and vigorous stirring at room tempe rature.We revealed orga nic solvents used in the oxide synthesis had a considerable influence on its surface charge that was beneficial for a uniformly electrostatic self-decoration between positively charged p-type CuO nanoparticles and negatively charged n-type spherical SnO2.Interestingly,CuO was partially reduced to Cu metal during high concentration of toluene exposure destroying p-n contact and developing new metal-semiconductor contact so-called ohmic junction,resulting in extraordinarily responsive and selective to toluene gas at 400℃as compared to a single p-CuO and n-SnO2.It was also found that the amount of particle decoration had an influence on sensor response and resistance.The optimum amount of CuO nanoparticle decoration was0.1 mmol on 0.5 mmol SnO2.The re s ponse(S=Ra/Rg)and selectivity of CuO/S nO2 based material toward the exposure of 75 ppm toluene had reached to such high as 540 and 5,respectively.The effect of p-n heterojunction and metal-semiconductor contact on the gas sensing mechanism of p-type CuO/n-type SnO2 was discussed.Furthermore,by decorating with CuO nanoparticles,CuO/SnO2 morphology was well-maintained after gas sensing evaluation demonstrated its excellency for high temperature toluene gas sensor application.展开更多
基金financially supported by the Japan Society for the Promotion of Science(JSPS)Grant-in-Aid for the Scientific Research(KAKENHI)on Innovative Areas“Mixed Anion”(No.16H06439,No.16H06440)by the Dynamic Alliance for Open Innovations Bridging Human,Environment and Materials,the Cooperative Research Program of“Network Joint Research Center for Materials and Devices”。
文摘We reported a facile preparation of a uniform decoration of spherical n-type SnO2 by p-type CuO nanopa rticles as well as their utilization for enhanced performance on toluene gas detection.CuO nanoparticles and spherical SnO2 were synthesized by a facile non-hydrolytic solvothermal reaction,which could easily control their morphology.A uniform CuO nanoparticles decoration onto spherical SnO2 was achieved by a simple sonication and vigorous stirring at room tempe rature.We revealed orga nic solvents used in the oxide synthesis had a considerable influence on its surface charge that was beneficial for a uniformly electrostatic self-decoration between positively charged p-type CuO nanoparticles and negatively charged n-type spherical SnO2.Interestingly,CuO was partially reduced to Cu metal during high concentration of toluene exposure destroying p-n contact and developing new metal-semiconductor contact so-called ohmic junction,resulting in extraordinarily responsive and selective to toluene gas at 400℃as compared to a single p-CuO and n-SnO2.It was also found that the amount of particle decoration had an influence on sensor response and resistance.The optimum amount of CuO nanoparticle decoration was0.1 mmol on 0.5 mmol SnO2.The re s ponse(S=Ra/Rg)and selectivity of CuO/S nO2 based material toward the exposure of 75 ppm toluene had reached to such high as 540 and 5,respectively.The effect of p-n heterojunction and metal-semiconductor contact on the gas sensing mechanism of p-type CuO/n-type SnO2 was discussed.Furthermore,by decorating with CuO nanoparticles,CuO/SnO2 morphology was well-maintained after gas sensing evaluation demonstrated its excellency for high temperature toluene gas sensor application.
