Azole derivatives such as 2-mercaptobenzothiazole(MBT) and 2-mercaptobenzimidazole(MBI) were introduced as corrosion inhibitors into the interlayer space of sodium montmorillonite clay(Na+-MMT). The corrosion protecti...Azole derivatives such as 2-mercaptobenzothiazole(MBT) and 2-mercaptobenzimidazole(MBI) were introduced as corrosion inhibitors into the interlayer space of sodium montmorillonite clay(Na+-MMT). The corrosion protection behavior of mild steel in solutions containing MBT, MBI, MMT + MBT, MMT + MBI, Na^+-MMT, and NaCl(3.5 wt%) was evaluated using polarization and electrochemical impedance spectroscopy(EIS). Also, the release of penetrated species into the medium from the clay nanocarriers was evaluated using ultraviolet-visible(UV-Vis) spectroscopy. Small-angle X-ray scattering(SAXS) confirmed the insertion of MBT and MBI into the inner space of the clay layers and the interaction between two organic and inorganic phases. Scanning electron microscopy(SEM) was used to assess the morphology of the surface of the steel samples after the samples had been immersed for 24 h in the extraction solution. The corrosion protection in the solutions with clay nanocarriers containing MBT and MBI was better than that in solutions without MMT. The UV-Vis results showed that the release of MBI species from Na+-MMT nanocarriers in neutral pH was far lower than that of MBT species.展开更多
Nano-clay based pigments (NCP) are new type of pigments composed of organic dyes and layered silicate- clay nano-particles, and have already been used in polymeric coatings to improve mechanical thermal and stabilit...Nano-clay based pigments (NCP) are new type of pigments composed of organic dyes and layered silicate- clay nano-particles, and have already been used in polymeric coatings to improve mechanical thermal and stability properties. In this paper, the basic blue 41(BB41) was intercalated into Na+- montmorillonite in an aqueous medium. The dye-intercalated montmorillonite was cen- trifuged, dried, and milled to prepare the nanopigrnent particles. X-ray diffraction showed an increase in the basal spacing, thus confirming intercalation of the BB41 molecules within the nanostructures of the interlayer spaces. Fourier transform infrared spectroscopy was used for identifying the functional groups and chemical bounding of Na+-montmorillonite, BB41 and montmor- illonite-BB41. The morphology of NCP was also studied by transmission electron microscopy. Finally, thermo- gravimetric analysis and differential thermograms sug- gested the thermal stability of the intercalated dye was improved.展开更多
The Editors-in-Chief retract the above-mentioned article. Upon investigation carried out according to the Committee on Publication Ethics guidelines on plagiarism, it has been found that the authors have duplicated su...The Editors-in-Chief retract the above-mentioned article. Upon investigation carried out according to the Committee on Publication Ethics guidelines on plagiarism, it has been found that the authors have duplicated substantial parts from the following article: Intercalation of methylene blue into montmorillonite at different conditions: An approach for preparing clay-based nanopigments. Validi M, Bazgir S, Rashidi A, Yazdanshenas M E, Ceramics-Silikaty, 2012, 56(2): 152-158, INST CHEMICAL TECHNOLOGY, DEPT CLASS CERAMICS. The Editors-in-Chief take issues of research and publication misconduct seriously in order to preserve the integrity of the academic record.展开更多
文摘Azole derivatives such as 2-mercaptobenzothiazole(MBT) and 2-mercaptobenzimidazole(MBI) were introduced as corrosion inhibitors into the interlayer space of sodium montmorillonite clay(Na+-MMT). The corrosion protection behavior of mild steel in solutions containing MBT, MBI, MMT + MBT, MMT + MBI, Na^+-MMT, and NaCl(3.5 wt%) was evaluated using polarization and electrochemical impedance spectroscopy(EIS). Also, the release of penetrated species into the medium from the clay nanocarriers was evaluated using ultraviolet-visible(UV-Vis) spectroscopy. Small-angle X-ray scattering(SAXS) confirmed the insertion of MBT and MBI into the inner space of the clay layers and the interaction between two organic and inorganic phases. Scanning electron microscopy(SEM) was used to assess the morphology of the surface of the steel samples after the samples had been immersed for 24 h in the extraction solution. The corrosion protection in the solutions with clay nanocarriers containing MBT and MBI was better than that in solutions without MMT. The UV-Vis results showed that the release of MBI species from Na+-MMT nanocarriers in neutral pH was far lower than that of MBT species.
文摘Nano-clay based pigments (NCP) are new type of pigments composed of organic dyes and layered silicate- clay nano-particles, and have already been used in polymeric coatings to improve mechanical thermal and stability properties. In this paper, the basic blue 41(BB41) was intercalated into Na+- montmorillonite in an aqueous medium. The dye-intercalated montmorillonite was cen- trifuged, dried, and milled to prepare the nanopigrnent particles. X-ray diffraction showed an increase in the basal spacing, thus confirming intercalation of the BB41 molecules within the nanostructures of the interlayer spaces. Fourier transform infrared spectroscopy was used for identifying the functional groups and chemical bounding of Na+-montmorillonite, BB41 and montmor- illonite-BB41. The morphology of NCP was also studied by transmission electron microscopy. Finally, thermo- gravimetric analysis and differential thermograms sug- gested the thermal stability of the intercalated dye was improved.
文摘The Editors-in-Chief retract the above-mentioned article. Upon investigation carried out according to the Committee on Publication Ethics guidelines on plagiarism, it has been found that the authors have duplicated substantial parts from the following article: Intercalation of methylene blue into montmorillonite at different conditions: An approach for preparing clay-based nanopigments. Validi M, Bazgir S, Rashidi A, Yazdanshenas M E, Ceramics-Silikaty, 2012, 56(2): 152-158, INST CHEMICAL TECHNOLOGY, DEPT CLASS CERAMICS. The Editors-in-Chief take issues of research and publication misconduct seriously in order to preserve the integrity of the academic record.