New Methods Testing of Adhesion of the Coating to Sheet Metal by Bending

The article is deals for new experimental equipment for effective test adhesion for selected coating STEEL, applied cold on the coated metal sheet with Al (aluminum). Explanation to the word STEEL: STEEL coating has significant anti- corrosive properties and he is resistant for main oxidizing agents such as acids, alkalis, salt vapors etc. Resists tem- peratures to 600?C and create an elastic film that is resistant to abrasion, as soon as it was to complete po-lymerization. It is very simple to applied to metallic and nonmetallic surfaces. Dries quickly and is dry to the touch after 90 to 120 seconds. STEEL is the best possible solution anywhere, if needs arises powerful local protection against atmospheric and corrosive agents or to elevated temperatures. STEEL is also useful as a method for protect of welds on stainless steels instead of traditional staining procedures. Broad application is in automotive industry to modify the surfaces of block vehicle, car-body repairs, welds needing protection, in heating industry for example boilers, in air condition with heat exchanger and in shipping industry. [1-3].In experiments with a new test equipment is showed that for bending radius of interval from range R11 to R35 there is a change deposited coating STEEL from original coating Al and this coating was part of test metal sheet of thickness 1.5 mm. In the next stage of solution was developed technological process, which allowed increase of adhesion coating STEEL for bending up to or maximum 180? (shape U). Result of new technology is documented in article. Experiments was implementing with cooperation of the Masaryk University in Brno.

Study of Deformation Coating for Sheets by Using Tensile Test

This article focuses on the study of the defined values of tensile strain and the effect of low temperature plasma adhesion selected coatings on steel samples using a tensile testing flat test bars. Samples were made by machining and welding technologies. The flat test bars were tested by pulling on a test rig UPC 1200. Part of the samples was treated on the surface prior to coating by a tensile test, second base coat and with a final coat continuous multi plasma system. The selected test samples were determined from the tensile test of the material characteristics apparent from the tensile diagrams. The examined samples were fitted top and base coat. Another group was the KTL basis. The presented graphs show the dependence of the strength on elongation of a sample according to DIN EN ISO 6892-2. The samples were then examined under a stereo microscope SCHUT brand, type SSM-E in the laboratory to conduct coating on a steel sheet at the moment of total violation sectional samples. The base layer, in which the temperature ranges from 160°C - 180°C, was applied by electrophoresis method.