After finishing 102 replicate constant amplitude crack initiation and growth tests on Ly12-CZ aluminum alloy plate, a statistical investigation of the fatigue crack initiation and growth process is conducted in this p...After finishing 102 replicate constant amplitude crack initiation and growth tests on Ly12-CZ aluminum alloy plate, a statistical investigation of the fatigue crack initiation and growth process is conducted in this paper. According to the post-mortem fractographic examination by scanning electron microscopy (SEM), some qualitative observations of the spacial correlation among fatigue striations are developed to reveal the statistical nature of material intrinsic inhomogeneity during the crack growth process. From the test data, an engineering division between crack initiation and growth is defined as the upper limit of small crack. The distributions of crack initiation life N-i, growth life N, and the statistical characteristics of crack growth rate da/dN are also investigated. It is hoped that the work will provide a solid test basis for the study of probabilistic fatigue, probabilistic fracture mechanics, fatigue reliability and its engineering applications.展开更多
基金The project is supported by the Aeronautic Science Foundation,China
文摘After finishing 102 replicate constant amplitude crack initiation and growth tests on Ly12-CZ aluminum alloy plate, a statistical investigation of the fatigue crack initiation and growth process is conducted in this paper. According to the post-mortem fractographic examination by scanning electron microscopy (SEM), some qualitative observations of the spacial correlation among fatigue striations are developed to reveal the statistical nature of material intrinsic inhomogeneity during the crack growth process. From the test data, an engineering division between crack initiation and growth is defined as the upper limit of small crack. The distributions of crack initiation life N-i, growth life N, and the statistical characteristics of crack growth rate da/dN are also investigated. It is hoped that the work will provide a solid test basis for the study of probabilistic fatigue, probabilistic fracture mechanics, fatigue reliability and its engineering applications.