Metallic Pd clusters were embedded into TiO2 nanoparticles that were synthesized within reverse micelle via a solution reduction of Pd(NO3)2 by hydrazine hydrate. The size of the particles can be controlled by manipul...Metallic Pd clusters were embedded into TiO2 nanoparticles that were synthesized within reverse micelle via a solution reduction of Pd(NO3)2 by hydrazine hydrate. The size of the particles can be controlled by manipulating the relative rates of the hydrolysis and condensation reactions of titanium tetra-isopropoxide within the micro-emulsion. The spherical equivalent size for the Pd clusters formed in TiO2 matrix was estimated to be around (3±1) nm. The presence of Pd in the matrix was demonstrated by EDS spectroscopy. The effects of synthesis parameters, such as the concentration of Pd solution, the molar ratio of water to TIP, and the molar ratio of water to surfactant, were discussed.展开更多
The nanosized Ba(CoxNb1-x)O3(BCN) particles were prepared under high temperature and pressure conditions by precipitation from metal nitrates with aqueous potassium hydroxide. Ba(CoxNb1-x)O3 powders were obtained in t...The nanosized Ba(CoxNb1-x)O3(BCN) particles were prepared under high temperature and pressure conditions by precipitation from metal nitrates with aqueous potassium hydroxide. Ba(CoxNb1-x)O3 powders were obtained in the temperature range of 170-210 ℃ for 6 h. The results show that the average size of the synthesized particles increases with increasing reaction temperature. The average size of the synthesized particles is about 10 nm. The crystalline phase of the synthesized particles is found to be Ba(CoxNb1-x)O3. Ceramics derived from the nano BCN powders could achieve high sintering density at a relatively low sintering temperature.展开更多
In the present study hydroxyapatite （HA） nano-hexagonal rods with 70-90 nm diameter and 400-500 nm length are synthesized using a simple sol-gel route with calcium nitrate and potassium dihydrogenphosphate as calciu...In the present study hydroxyapatite （HA） nano-hexagonal rods with 70-90 nm diameter and 400-500 nm length are synthesized using a simple sol-gel route with calcium nitrate and potassium dihydrogenphosphate as calcium and phosphorus precursors respectively. Deionized water was used as a diluting media for HA sol preparation and ammonia was used to adjust the pH = 9. After aging, the HA gel was dried at 60 ℃ and calcined at different temperatures ranging from 300 to 700 ℃. The dried and calcined powders were characterized for phase composition using X-ray diffractrometry, elemental dispersive X-ray and Fourier transform infrared spectroscopy. Rietveld analysis showed the calcined HA powders of high purity with a hexagonal unit cell structure. Calcination yielded HA nanopowders of increased particle size and crystallinity with increase in temperature. The particle size and morphology was studied using transmission electron microscopy. The aspect ratio （length to diameter ratio） of HA nanorods was measured to be between 6 and 7.展开更多
基金supported by the Ministry of Education,Science Technology(MEST) and Korea Industrial Technology Foundation(KOTEF) through the Human Resource Training Project for Regional Innovation
文摘Metallic Pd clusters were embedded into TiO2 nanoparticles that were synthesized within reverse micelle via a solution reduction of Pd(NO3)2 by hydrazine hydrate. The size of the particles can be controlled by manipulating the relative rates of the hydrolysis and condensation reactions of titanium tetra-isopropoxide within the micro-emulsion. The spherical equivalent size for the Pd clusters formed in TiO2 matrix was estimated to be around (3±1) nm. The presence of Pd in the matrix was demonstrated by EDS spectroscopy. The effects of synthesis parameters, such as the concentration of Pd solution, the molar ratio of water to TIP, and the molar ratio of water to surfactant, were discussed.
基金supported by the Ministry of Education,Science Technology (MEST) and Korea Industrial Technology Foundation (KOTEF) through the Human Resource Training Project for Regional Innovation
文摘The nanosized Ba(CoxNb1-x)O3(BCN) particles were prepared under high temperature and pressure conditions by precipitation from metal nitrates with aqueous potassium hydroxide. Ba(CoxNb1-x)O3 powders were obtained in the temperature range of 170-210 ℃ for 6 h. The results show that the average size of the synthesized particles increases with increasing reaction temperature. The average size of the synthesized particles is about 10 nm. The crystalline phase of the synthesized particles is found to be Ba(CoxNb1-x)O3. Ceramics derived from the nano BCN powders could achieve high sintering density at a relatively low sintering temperature.
文摘In the present study hydroxyapatite （HA） nano-hexagonal rods with 70-90 nm diameter and 400-500 nm length are synthesized using a simple sol-gel route with calcium nitrate and potassium dihydrogenphosphate as calcium and phosphorus precursors respectively. Deionized water was used as a diluting media for HA sol preparation and ammonia was used to adjust the pH = 9. After aging, the HA gel was dried at 60 ℃ and calcined at different temperatures ranging from 300 to 700 ℃. The dried and calcined powders were characterized for phase composition using X-ray diffractrometry, elemental dispersive X-ray and Fourier transform infrared spectroscopy. Rietveld analysis showed the calcined HA powders of high purity with a hexagonal unit cell structure. Calcination yielded HA nanopowders of increased particle size and crystallinity with increase in temperature. The particle size and morphology was studied using transmission electron microscopy. The aspect ratio （length to diameter ratio） of HA nanorods was measured to be between 6 and 7.