This paper provides a new system and concept concerning to MEMS air turbine power generator. The generator was composed of the MEMS air turbine and the magnetic circuit. The magnetic circuit was fabricated by multilay...This paper provides a new system and concept concerning to MEMS air turbine power generator. The generator was composed of the MEMS air turbine and the magnetic circuit. The magnetic circuit was fabricated by multilayer magnetic ceramic technology and achieved monolithic structure which included high permeability material and three di-mensional helical conductor patterns inside. Although the output power was micro watt class, some features were extracted by comparing to the simple winding wire type magnetic circuit. In the power density measurement, almost same output power density was extracted though the turn number of the winding wire type was more than that of monolithic type. Also the resistance of the conductor was quarter of the winding type. The maximum output voltage and the maximum power of the monolithic generator was 6.2 mV and 1.92 μVA respectively. The DC conductor resistance was 1.2 Ω. The energy density was 0.046 μVA/mm3. The appearance size of the monolithic type was 3.6, 3.4, 3.5 mm, length, width and height respectively.展开更多
Patterning technology of ferrite and insulating material in multilayer ceramic devices is proposed. In the conventional technology, the different ceramic materials such as the ferrite and the insulating material have ...Patterning technology of ferrite and insulating material in multilayer ceramic devices is proposed. In the conventional technology, the different ceramic materials such as the ferrite and the insulating material have been prepared in the form of the each different green sheet, and then they have been stacked each other. Otherwise the different material has filled cavities that were formed by a mechanical punching in advanced. In our proposing technology, arbitrary patterning of the different ceramic material inside the same green sheet is possible. In this process, the arbitrary shape of the through pattern is formed in the green sheet of the base material by making use of photo resist films as sacrifice patterns, and then the base material is masked by the patterned photo resist film. After filling the slurry of the different material into the through pattern of the base material passing the resist mask, the pattern of the different ceramic material in the green sheet is achieved. In the present paper, the ferrite magnetic material and the alumina-glass composite material are used. The patterned structure inside the green sheet is obtained. The slurry preparation, the thickness of the mask resist film, and the obtained structure of the green sheet are discussed.展开更多
文摘This paper provides a new system and concept concerning to MEMS air turbine power generator. The generator was composed of the MEMS air turbine and the magnetic circuit. The magnetic circuit was fabricated by multilayer magnetic ceramic technology and achieved monolithic structure which included high permeability material and three di-mensional helical conductor patterns inside. Although the output power was micro watt class, some features were extracted by comparing to the simple winding wire type magnetic circuit. In the power density measurement, almost same output power density was extracted though the turn number of the winding wire type was more than that of monolithic type. Also the resistance of the conductor was quarter of the winding type. The maximum output voltage and the maximum power of the monolithic generator was 6.2 mV and 1.92 μVA respectively. The DC conductor resistance was 1.2 Ω. The energy density was 0.046 μVA/mm3. The appearance size of the monolithic type was 3.6, 3.4, 3.5 mm, length, width and height respectively.
文摘Patterning technology of ferrite and insulating material in multilayer ceramic devices is proposed. In the conventional technology, the different ceramic materials such as the ferrite and the insulating material have been prepared in the form of the each different green sheet, and then they have been stacked each other. Otherwise the different material has filled cavities that were formed by a mechanical punching in advanced. In our proposing technology, arbitrary patterning of the different ceramic material inside the same green sheet is possible. In this process, the arbitrary shape of the through pattern is formed in the green sheet of the base material by making use of photo resist films as sacrifice patterns, and then the base material is masked by the patterned photo resist film. After filling the slurry of the different material into the through pattern of the base material passing the resist mask, the pattern of the different ceramic material in the green sheet is achieved. In the present paper, the ferrite magnetic material and the alumina-glass composite material are used. The patterned structure inside the green sheet is obtained. The slurry preparation, the thickness of the mask resist film, and the obtained structure of the green sheet are discussed.