In the stainless steel 304 （SUS 304） wire drawing process, optimizing the die life and wire tensile strength, which are the larger-the-better quality characteristics （QCH） types, is of main interest. Three control...In the stainless steel 304 （SUS 304） wire drawing process, optimizing the die life and wire tensile strength, which are the larger-the-better quality characteristics （QCH） types, is of main interest. Three control factors, involving reduction ratio, lubricant temperature, and drawing speed, were investigated utilizing L9（34） orthogonal array （OA）. The grey relational analysis was conducted for the normalized signal-to-noise （S/N） ratios. The ordinal value of the grey grade was then used to decide optimal factor levels. The anticipated improvements in die life and wire tensile strength were estimated 25.31 h and 22.50 kg/mm2, respectively. To decide the significant factor which had effect on each QCH and predict the average value of each QCH, analysis of variance （ANOVA） was performed for S/N ratio and QCH. Confirmation experiments were then conducted, where a good overlap was noticed between the predicted and confirnation intervals for each QCH. The Hotelling T2 and the sample generalized variance control charts were finally utilized in controlling and monitoring future production. In conclusion, the grey relational analysis utilizing Taguchi method is an effective approach for optimizing the die life and wire tensile strength for SUS wire drawing process. 2008 University of Science and Technology Beijing. All rights reserved.展开更多
We investigated optically controllable gray-level diffraction from a body-centered tetragonal photonic crystal that was based on an azo-dye-doped holographic polymer dispersed liquid crystal. The sample is fabricated ...We investigated optically controllable gray-level diffraction from a body-centered tetragonal photonic crystal that was based on an azo-dye-doped holographic polymer dispersed liquid crystal. The sample is fabricated by use of two-beam interference with multi-exposure. Bichromatic pumping beams at various intensities were used to pump the sample to change the concentration of the cis isomer and, in turn, modulate the effective index of the photonic crystals as well as their diffraction intensity. Three pumping processes were utilized to produce gray-level switching of diffractive light. This study demonstrates the optimum gray-level to be 15-level of up-step and down-step. The simulation of the diffraction intensity under bichromatic pumping sources was also studied.展开更多
文摘In the stainless steel 304 （SUS 304） wire drawing process, optimizing the die life and wire tensile strength, which are the larger-the-better quality characteristics （QCH） types, is of main interest. Three control factors, involving reduction ratio, lubricant temperature, and drawing speed, were investigated utilizing L9（34） orthogonal array （OA）. The grey relational analysis was conducted for the normalized signal-to-noise （S/N） ratios. The ordinal value of the grey grade was then used to decide optimal factor levels. The anticipated improvements in die life and wire tensile strength were estimated 25.31 h and 22.50 kg/mm2, respectively. To decide the significant factor which had effect on each QCH and predict the average value of each QCH, analysis of variance （ANOVA） was performed for S/N ratio and QCH. Confirmation experiments were then conducted, where a good overlap was noticed between the predicted and confirnation intervals for each QCH. The Hotelling T2 and the sample generalized variance control charts were finally utilized in controlling and monitoring future production. In conclusion, the grey relational analysis utilizing Taguchi method is an effective approach for optimizing the die life and wire tensile strength for SUS wire drawing process. 2008 University of Science and Technology Beijing. All rights reserved.
文摘We investigated optically controllable gray-level diffraction from a body-centered tetragonal photonic crystal that was based on an azo-dye-doped holographic polymer dispersed liquid crystal. The sample is fabricated by use of two-beam interference with multi-exposure. Bichromatic pumping beams at various intensities were used to pump the sample to change the concentration of the cis isomer and, in turn, modulate the effective index of the photonic crystals as well as their diffraction intensity. Three pumping processes were utilized to produce gray-level switching of diffractive light. This study demonstrates the optimum gray-level to be 15-level of up-step and down-step. The simulation of the diffraction intensity under bichromatic pumping sources was also studied.
