To develop an improved approach in achieving an excellent combination of high strength and ductility,the solutionized Al?Cu?Li plates were subjected to rolling at cryogenic and room temperatures,respectively,to a redu...To develop an improved approach in achieving an excellent combination of high strength and ductility,the solutionized Al?Cu?Li plates were subjected to rolling at cryogenic and room temperatures,respectively,to a reduction of83%,followed by aging treatment at160°C.The results indicate that Al?Cu?Li alloys through cryogenic rolling followed by aging treatment possess better mechanical properties.Rolling at cryogenic temperature produces a high density of dislocations because of the suppression of dynamic recovery,which in turn promotes the precipitation of T1(Al2CuLi)precipitates during aging.Such high density of T1precipitates enable effective dislocation pinning,leading to an increase in strength and ductility.In contrast,room temperature rolled alloys after aging treatment exhibit lower strength and ductility due to low density of T1precipitates in the grain interior and high density of T1precipitates around subgrain boundaries.展开更多
基金Projects (106112015CDJXZ138803,106112015CDJXY130003) supported by the Fundamental Research Funds for the Central Universities,ChinaProject (51421001) supported by National Natural Science Foundation of China
文摘To develop an improved approach in achieving an excellent combination of high strength and ductility,the solutionized Al?Cu?Li plates were subjected to rolling at cryogenic and room temperatures,respectively,to a reduction of83%,followed by aging treatment at160°C.The results indicate that Al?Cu?Li alloys through cryogenic rolling followed by aging treatment possess better mechanical properties.Rolling at cryogenic temperature produces a high density of dislocations because of the suppression of dynamic recovery,which in turn promotes the precipitation of T1(Al2CuLi)precipitates during aging.Such high density of T1precipitates enable effective dislocation pinning,leading to an increase in strength and ductility.In contrast,room temperature rolled alloys after aging treatment exhibit lower strength and ductility due to low density of T1precipitates in the grain interior and high density of T1precipitates around subgrain boundaries.