The formation mechanisms and growth kinetics of Al3 Ni and Al3Ni2 in Ni-Al diffusion couple prepared by electrodeposition of Ni on Al substrate were investigated. The nickel coating with 20 μm thickness was applied o...The formation mechanisms and growth kinetics of Al3 Ni and Al3Ni2 in Ni-Al diffusion couple prepared by electrodeposition of Ni on Al substrate were investigated. The nickel coating with 20 μm thickness was applied on 6061 aluminum alloy by direct current electroplating. The samples were then heat-treated for different durations at 450, 500 and 550 °C under argon atmosphere. The intermetallic phases were identified by means of scanning electron microscopy（SEM）, energy dispersive spectrometry（EDS） and X-ray diffraction（XRD）. The results showed that the formation of intermetallic phases consisted of two important steps. The first step was the lateral growth of intermetallic phase from separate sites, resulting in the formation of a continuous layer. The second step was the growth of the continuous intermetallic layer in the direction perpendicular to the interface. However, excessive increase in thickness of intermetallic phases led to the detachment of reaction products, i.e., Al3 Ni and Al3Ni2, from the substrate. It was also observed that aluminum was the dominant diffusing element during Al3 Ni growth, while nickel diffusion was dominant during Al3Ni2 growth. The growth kinetics of both Al3 Ni and Al3Ni2 phases obeyed a parabolic law.展开更多
Ni-Al composite coatings were electrodeposited from a modified Watts solution. The electrochemical behavior of the coatings was studied by means of zeta potential analysis, voltammetry and electrochemical impedance sp...Ni-Al composite coatings were electrodeposited from a modified Watts solution. The electrochemical behavior of the coatings was studied by means of zeta potential analysis, voltammetry and electrochemical impedance spectroscopy（EIS）. It was found that the zeta potential of Al particles was-4 m V which is very close to that of Al2O3. Moreover, addition of conductive Al particles into the electrolyte shifted the polarization curve to more negative potentials and loop size of EIS curve increased. It was also demonstrated that the co-deposition behavior of Ni-Al composite coatings obeys the Guglielmi’s model. The results indicate that conductive Al particles behave as the inert particles and confirm the existence of a thin aluminum oxide layer on the surface of aluminum particles.展开更多
文摘The formation mechanisms and growth kinetics of Al3 Ni and Al3Ni2 in Ni-Al diffusion couple prepared by electrodeposition of Ni on Al substrate were investigated. The nickel coating with 20 μm thickness was applied on 6061 aluminum alloy by direct current electroplating. The samples were then heat-treated for different durations at 450, 500 and 550 °C under argon atmosphere. The intermetallic phases were identified by means of scanning electron microscopy（SEM）, energy dispersive spectrometry（EDS） and X-ray diffraction（XRD）. The results showed that the formation of intermetallic phases consisted of two important steps. The first step was the lateral growth of intermetallic phase from separate sites, resulting in the formation of a continuous layer. The second step was the growth of the continuous intermetallic layer in the direction perpendicular to the interface. However, excessive increase in thickness of intermetallic phases led to the detachment of reaction products, i.e., Al3 Ni and Al3Ni2, from the substrate. It was also observed that aluminum was the dominant diffusing element during Al3 Ni growth, while nickel diffusion was dominant during Al3Ni2 growth. The growth kinetics of both Al3 Ni and Al3Ni2 phases obeyed a parabolic law.
文摘Ni-Al composite coatings were electrodeposited from a modified Watts solution. The electrochemical behavior of the coatings was studied by means of zeta potential analysis, voltammetry and electrochemical impedance spectroscopy（EIS）. It was found that the zeta potential of Al particles was-4 m V which is very close to that of Al2O3. Moreover, addition of conductive Al particles into the electrolyte shifted the polarization curve to more negative potentials and loop size of EIS curve increased. It was also demonstrated that the co-deposition behavior of Ni-Al composite coatings obeys the Guglielmi’s model. The results indicate that conductive Al particles behave as the inert particles and confirm the existence of a thin aluminum oxide layer on the surface of aluminum particles.