Abstract: We performed fluidized bed coating ofAl-based nanoeomposite powder-binder suspensions onto polymer substrates. The effects of the type and amount of the binder and nanoparticle additive on the coating proce...Abstract: We performed fluidized bed coating ofAl-based nanoeomposite powder-binder suspensions onto polymer substrates. The effects of the type and amount of the binder and nanoparticle additive on the coating process efficiency and coating characteristics were investigated. The efficiency decreased from 52% to 49% as the processing time increased from 15 to 20 min. However, the amount and thickness of the coating also increased as the processing time and amount of the binder were increased. The addition of nanoparticles to the system decreased the thickness of the coating from 222 to 207 μm when polyvinyl alcohol (PVA) was used as a binder. The suspension containing 3wt% R-4410 binder exhibited the greatest efficiency of 60%.展开更多
The properties orAl based nanocomposite metal foams and their corrosion behaviors were investigated in this study. For this, the composite metal foams with different relative densities (porosity) reinforced with alu...The properties orAl based nanocomposite metal foams and their corrosion behaviors were investigated in this study. For this, the composite metal foams with different relative densities (porosity) reinforced with alumina nanoparticles were prepared using a powder me- tallurgy-based sintering-dissolution process (SDP) and NaC1 particles were used as space holders. Then, the effect of nanoparticle rein- forcement and different amounts of NaC1 space holders (corresponding porosity) on the microstructure, morphology, density, hardness, and electrochemical specifications of the samples were investigated. It was found that as the relative density increased from 60% to 70%, the wall thickness increased from about 200 to 300 pro, which led to a decrease in pore size. Also, the addition of nanoparticle reinforcement and the increased relative density result in increasing metal foam hardness. Moreover, electrochemical test results indicated that increasing the A1203 content reduced the corrosion rate, but increasing the porosity enhanced it.展开更多
文摘Abstract: We performed fluidized bed coating ofAl-based nanoeomposite powder-binder suspensions onto polymer substrates. The effects of the type and amount of the binder and nanoparticle additive on the coating process efficiency and coating characteristics were investigated. The efficiency decreased from 52% to 49% as the processing time increased from 15 to 20 min. However, the amount and thickness of the coating also increased as the processing time and amount of the binder were increased. The addition of nanoparticles to the system decreased the thickness of the coating from 222 to 207 μm when polyvinyl alcohol (PVA) was used as a binder. The suspension containing 3wt% R-4410 binder exhibited the greatest efficiency of 60%.
文摘The properties orAl based nanocomposite metal foams and their corrosion behaviors were investigated in this study. For this, the composite metal foams with different relative densities (porosity) reinforced with alumina nanoparticles were prepared using a powder me- tallurgy-based sintering-dissolution process (SDP) and NaC1 particles were used as space holders. Then, the effect of nanoparticle rein- forcement and different amounts of NaC1 space holders (corresponding porosity) on the microstructure, morphology, density, hardness, and electrochemical specifications of the samples were investigated. It was found that as the relative density increased from 60% to 70%, the wall thickness increased from about 200 to 300 pro, which led to a decrease in pore size. Also, the addition of nanoparticle reinforcement and the increased relative density result in increasing metal foam hardness. Moreover, electrochemical test results indicated that increasing the A1203 content reduced the corrosion rate, but increasing the porosity enhanced it.