This paper addressed the efect of copper acetate on the combustion characteristics of anthracite depending on the fractional composition of fuel and additive introduction method.Anthracite was impregnated with 5 wt%of...This paper addressed the efect of copper acetate on the combustion characteristics of anthracite depending on the fractional composition of fuel and additive introduction method.Anthracite was impregnated with 5 wt%of Cu(CH_(3)COO)_(2)by mechanical mixing and incipient wetness impregnation.Four anthracite samples of diferent fraction with d<0.1 mm,d=0.1-0.5 mm,d=0.5-1.0 mm,and d=1.0-2.0 mm were compared.According to EDX mapping,incipient wetness impregnation provides a higher dispersion of the additive and its uniform distribution in the sample.The ignition and combustion characteristics of the modifed anthracite samples were studied by thermal analysis and high-speed video recording of the processes in a combustion chamber(at heating medium temperature of 800℃).It was found that copper acetate increases anthracite reactivity,which was evidenced by decreased onset temperature of combustion(ΔT_(i))by 35-190℃and reduced ignition delay time(Δτ_(i))by 2.1-5.4 s.Copper acetate reduces fuel underburning(on average by 70%)in the ash residue of anthracite and decreases the amount of CO and NO_(x)in gas-phase products(on average by 18.5%and 20.8%,respectively).The mechanism for activation of anthracite combustion by copper acetate is proposed.展开更多
文摘This paper addressed the efect of copper acetate on the combustion characteristics of anthracite depending on the fractional composition of fuel and additive introduction method.Anthracite was impregnated with 5 wt%of Cu(CH_(3)COO)_(2)by mechanical mixing and incipient wetness impregnation.Four anthracite samples of diferent fraction with d<0.1 mm,d=0.1-0.5 mm,d=0.5-1.0 mm,and d=1.0-2.0 mm were compared.According to EDX mapping,incipient wetness impregnation provides a higher dispersion of the additive and its uniform distribution in the sample.The ignition and combustion characteristics of the modifed anthracite samples were studied by thermal analysis and high-speed video recording of the processes in a combustion chamber(at heating medium temperature of 800℃).It was found that copper acetate increases anthracite reactivity,which was evidenced by decreased onset temperature of combustion(ΔT_(i))by 35-190℃and reduced ignition delay time(Δτ_(i))by 2.1-5.4 s.Copper acetate reduces fuel underburning(on average by 70%)in the ash residue of anthracite and decreases the amount of CO and NO_(x)in gas-phase products(on average by 18.5%and 20.8%,respectively).The mechanism for activation of anthracite combustion by copper acetate is proposed.