60CeO2-40TiO2 thin films were deposited on soda-lime silicate glass substrates by R.F. magnetron sputtering. The effects of heat-treatment on the UV-absorption of the thin films were studied on the 60CeO2-40TiO2 thin ...60CeO2-40TiO2 thin films were deposited on soda-lime silicate glass substrates by R.F. magnetron sputtering. The effects of heat-treatment on the UV-absorption of the thin films were studied on the 60CeO2-40TiO2 thin film with the largest UV cut-off wavelength. The sample films with CeO2：TiO2=60：40 were heated at 773 K, 873 K, 973 K for 30 min. These films are characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and X-ray photoelectron spectroscopy and spectrometer （XPS）. XRD analysis proves that the addition of TiO2 to CeO2 changed the crystalline state of CeO2. But the UV absorption effect of CeO2-TiO2 films with CeO2 crystallite phase is inferior to that of the amorphous phase CeO2-TiO2 films. XPS analysis also indicates that the amorphous phase CeO2-TiO2 films have the most Ce3＋ content in these films. Amorphous phase and crystalline phase of the CeO2-TiO2 films have different effects on UV absorption of the thin films.展开更多
基金the National Natural Science Foundation of China(No.51032005)the Fundamental Research Funds for the Central Universities(Wuhan University of Technology)+1 种基金the China Postdoctoral Science Foundation(No.2012M511285)the Fund for the Young Innovative Team(Hubei University of Education)(No.2012KQ05)
文摘60CeO2-40TiO2 thin films were deposited on soda-lime silicate glass substrates by R.F. magnetron sputtering. The effects of heat-treatment on the UV-absorption of the thin films were studied on the 60CeO2-40TiO2 thin film with the largest UV cut-off wavelength. The sample films with CeO2：TiO2=60：40 were heated at 773 K, 873 K, 973 K for 30 min. These films are characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and X-ray photoelectron spectroscopy and spectrometer （XPS）. XRD analysis proves that the addition of TiO2 to CeO2 changed the crystalline state of CeO2. But the UV absorption effect of CeO2-TiO2 films with CeO2 crystallite phase is inferior to that of the amorphous phase CeO2-TiO2 films. XPS analysis also indicates that the amorphous phase CeO2-TiO2 films have the most Ce3＋ content in these films. Amorphous phase and crystalline phase of the CeO2-TiO2 films have different effects on UV absorption of the thin films.