The BNT ceramic sample might be a good replacement for PZT piezoelectric in industrial applications,especially in energy harvesting from crystal vibrations.In order to enhance the performance of BNT ceramic,the solid ...The BNT ceramic sample might be a good replacement for PZT piezoelectric in industrial applications,especially in energy harvesting from crystal vibrations.In order to enhance the performance of BNT ceramic,the solid solution was chosen by substitution with Ba+2 at Morphtropic Phase Boundary(MPB).The BNT-xBT powders with x=1,0.07,0.06 and 0 were prepared by the hydrothermal method with average particle size(65–150 nm)at(90℃/72 h).The ceramic disc was sintered at(1150℃/4 h)and showed excellent relative density of about 96%.The results of X-ray diffraction(XRD)confirmed the MPB for x=0:06 and 0.07,while the BNT had a rhombohedral structure and BT had a tetragonal structure.The dielectric measurements showed that BNT,BNT-7BT,BNT-6BT behave as the relaxator ferroelectric and showed a strong dependence on frequency,especially in the MPB region while BT behaves as a normal ferroelectric.Both the Curie temperature and depolarization temperature decrease at the MPB region and showed strong dependency on frequency.展开更多
文摘The BNT ceramic sample might be a good replacement for PZT piezoelectric in industrial applications,especially in energy harvesting from crystal vibrations.In order to enhance the performance of BNT ceramic,the solid solution was chosen by substitution with Ba+2 at Morphtropic Phase Boundary(MPB).The BNT-xBT powders with x=1,0.07,0.06 and 0 were prepared by the hydrothermal method with average particle size(65–150 nm)at(90℃/72 h).The ceramic disc was sintered at(1150℃/4 h)and showed excellent relative density of about 96%.The results of X-ray diffraction(XRD)confirmed the MPB for x=0:06 and 0.07,while the BNT had a rhombohedral structure and BT had a tetragonal structure.The dielectric measurements showed that BNT,BNT-7BT,BNT-6BT behave as the relaxator ferroelectric and showed a strong dependence on frequency,especially in the MPB region while BT behaves as a normal ferroelectric.Both the Curie temperature and depolarization temperature decrease at the MPB region and showed strong dependency on frequency.